Tubular Ceramic Foam Via Polymeric Sponge Method
نویسندگان
چکیده
Tubular ceramic foams were prepared by using natural clay as starting material and 120 ppi polyurethane foam as template via polymeric sponge method. Samples were sintered with different temperatures from 1200°C to 1280°C. The result shows that 1250°C is the ideal sintering temperature where the highest compressive strength of 1.980MPa at 47.31% porosity is obtained. The highest value in compressive strength and the lowest percentage in porosity are attributed to the higher apparent density and crystallinity. These results lend support to the idea that the sintering temperature is important for the processing of tubular ceramic foam.
منابع مشابه
Foam-like scaffolds for bone tissue engineering based on a novel couple of silicate-phosphate specular glasses: synthesis and properties.
Glass-ceramic scaffolds mimicking the structure of cancellous bone were produced via sponge replication technique by using a polyurethane foam as template and glass powder below 30 lm as inorganic phase. Specifically, a SiO₂-based glass of complex composition and its corresponding P₂O₅-based "specular" glass were used as materials for scaffolding. The polymeric sponge was thermally removed and ...
متن کاملFabrication of hydroxyapatite-baghdadite nanocomposite scaffolds coated by PCL/Bioglass with polyurethane polymeric sponge technique
Objecttive (s): Silicate bioceramics like Baghdadite with chemical formula Ca3ZrSi2O9, has attracted the attention of researchers in biomedical field due to its remarkable in-vitro and in-vivo bioactivity and mechanical properties.Materials and Methods: Therefore, in the current study the baghdadite powder with Sol-Gel method was synthesized. Then, hydroxyapatite/Baghdadite (HA/Bagh) scaffolds ...
متن کاملHydroxyapatite-Hardystonite nanocomposite scaffolds prepared by the replacing the polyurethane polymeric sponge technique for tissue engineering applications
Objective (s): Silicate bioceramics containing Zn and Ca like hardystonite (Hr) with chemical formula Ca2ZnSi2O7 has attracted the attention of researchers in biomedical field due to its remarkable biological and mechanical properties. The new generation of bioceramics can applied in bone tissue engineering to substitute with infected bone. However, these zirconium-silicate bioceramics have pro...
متن کاملBioactive glass-derived trabecular coating: a smart solution for enhancing osteointegration of prosthetic elements.
In this work, the use of foam-like glass-ceramic scaffolds as trabecular coatings on ceramic prosthetic devices to enhance implant osteointegration is proposed. The feasibility of this innovative device was explored in a simplified, flat geometry: glass-ceramic scaffolds, prepared by polymeric sponge replication and mimicking the trabecular architecture of cancellous bone, were joined to alumin...
متن کاملResorbable glass-ceramic phosphate-based scaffolds for bone tissue engineering: synthesis, properties, and in vitro effects on human marrow stromal cells.
Highly porous bioresorbable glass-ceramic scaffolds were prepared via sponge replication method by using an open-cell polyurethane foam as a template and phosphate-based glass powders. The glass, belonging to the P2O5-SiO2-CaO-MgO-Na2O-K2O system, was synthesized by a melting-quenching route, ground, and sieved to obtain powders with a grain size of less than 30 μm. A slurry containing glass po...
متن کامل