A comparative analysis of Ag and Cu heat sink layers in L10-FePt films for heat-assisted magnetic recording
نویسندگان
چکیده
heat-assisted magnetic recording Robert Fernandez, Desalegne Teweldebrhan, Chen Zhang, Alexander Balandin, and Sakhrat Khizroev Center for 3-D Electronics, Department of Electrical Engineering, University of California—Riverside, Riverside, California 92521, USA Nano-Device Laboratory, Department of Electrical Engineering and Materials Science and Engineering Program, University of California—Riverside, Riverside, California 92521, USA
منابع مشابه
خواص مغناطیسی بلوری آلیاژ نانوذرات آهن- پلاتین (L10-FePt) در گذار فاز
High magneto- crystalline anisotropy (ku=7×106j/m3) of L10-FePt nanoparticles are an excellent candidate for ultra high-density magnetic recording. The 4 nm FePt nanocrystals were prepared by superhydride reduction of FeCl2·4H2O and Pt(acac)2 precursors in the phenyl ether by reduction of the 1, 2-hexadecanediol and LiBEt3H superhydride. The crystal and magnetic structures were studied by XRD a...
متن کاملModulation of preferred orientation and easy axis of magnetic anisotropy in L10 FePt films with Cu buffer layers
The crystallographic orientation and easy axis of magnetic anisotropy in L10 FePt films were successfully modulated with Cu buffer layers. The FePt film directly grown on the Cr90Mo10 underlayer showed a (001) preferred orientation with out-of-plane magnetic anisotropy. As the Cu buffer layer thickness was z4 nm, the FePt films showed a (110) preferred orientation with in-plane magnetic anisotr...
متن کاملInfluence of chemical ordering on the thermal conductivity and electronic relaxation in FePt thin films in heat assisted magnetic recording applications
We report on the out-of-plane thermal conductivities of tetragonal L10 FePt (001) easy-axis and cubic A1 FePt thin films via time-domain thermoreflectance over a temperature range from 133 K to 500 K. The out-of-plane thermal conductivity of the chemically ordered L10 phase with alternating Fe and Pt layers is ~23% greater than the thermal conductivity of the disordered A1 phase at room tempera...
متن کاملFirst-principles prediction of the morphology of L10 FePt nanoparticles supported on Mg(Ti)O for heat-assisted magnetic recording applications
We perform first-principles calculations to predict the morphology of L10 ordered FePt nanoparticles grown on Mg(Ti)O substrates with relevance to application in heat-assisted magnetic recording (HAMR) media. We show how incorporation of Ti into MgO substrates reduces the FePt adhesion energy from −1.29 (pure MgO) to −2.35 J/m2 (pure TiO). This effect is due to the formation of strong Fe-Ti bon...
متن کاملL 10 ordering and microstructure of FePt thin films with Cu , Ag , and Au additive
The influence of Cu, Ag, and Au additives on the L10 ordering, texture, and grain size of FePt thin films has been examined. Lattice parameter data indicated that Au and Ag additives tended to segregate from FePt, but Cu alloyed with FePt. FePt films with Au or Ag additive showed 1–2 kOe higher coercivity values compared to a pure FePt film after annealing at 450 °C and above for 10 min. The ad...