Fractographical Investigation of the Delamination under Fatigue Using Laser Confocal Electron Microscope
نویسندگان
چکیده
In this paper fracture surface of the fatigue delamination have been investigated. Fatigue delamination tests were performed on the crabon/epoxy under different stress ratios. Samples were cut from the DCB specimens and analyzed in Laser Confocal Scanning Microscope. The analysis was used to measure the roughness values. Different fractographic features observed in the study are discussed.
منابع مشابه
Experimental determination of probabilistic edge-delamination strength of a graphite–fiber/epoxy composite
Probabilistic edge-delamination strength of a thermosetting polymer composite was studied experimentally in this work. During the procedure, by means of edge-delamination tensile test, the graphite–fiber/epoxy laminate made of unidirectional Toray P7051S-20Q-1000 prepregs with an optimized lay-up of [122/–122/02]S was used for examining its probabilistic distributions of the edge-delamination o...
متن کاملExperimental determination of probabilistic edge-delamination strength of a graphiteâ•fifiber/epoxy composite
Probabilistic edge-delamination strength of a thermosetting polymer composite was studied experimentally in this work. During the procedure, by means of edge-delamination tensile test, the graphite–fiber/epoxy laminate made of unidirectional Toray P7051S-20Q-1000 prepregs with an optimized lay-up of [122/–122/02]S was used for examining its probabilistic distributions of the edge-delamination o...
متن کاملInvestigation on the Tribological Behavior and Wear Mechanism of Five Different Veneering Porcelains
OBJECTIVES The primary aim of this research was to investigate the wear behavior and wear mechanism of five different veneering porcelains. METHODS Five kinds of veneering porcelains were selected in this research. The surface microhardness of all the samples was measured with a microhardness tester. Wear tests were performed on a ball-on-flat PLINT fretting wear machine, with lubrication of ...
متن کاملInfluence of Ultrasonic Surface Rolling on Microstructure and Wear Behavior of Selective Laser Melted Ti-6Al-4V Alloy
The present article studied the effect of ultrasonic surface rolling process (USRP) on the microstructure and wear behavior of a selective laser melted Ti-6Al-4V alloy. Surface characteristics were investigated using optical microscope, nano-indentation, scanning electron microscope, transmission electron microscope and laser scanning confocal microscope. Results indicated that the thickness of...
متن کاملHigh-resolution three-dimensional tomographic diffractive microscopy of transparent inorganic and biological samples.
We have developed a tomographic diffractive microscope, equipped with a fluorescence confocal scanner. We measure experimentally the lateral resolution using an edge method and by comparing tomographic images of the same samples with wide-field and laser scanning confocal microscopy images; a scanning electron microscope image serves as a reference. The experimental resolution is shown to be to...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره شماره
صفحات -
تاریخ انتشار 2015