Transparent Oxyfluoride Nano-Glass Ceramics Doped with Pr3+ and Pr3+–Yb3+ for NIR Emission
نویسندگان
چکیده
1 Instituto de Cerámica y Vidrio, Consejo Superior de Investigaciones Científicas (CSIC), Madrid, Spain, 2 Microdevices for Photonics Laboratory (MIP-LAB), Istituto di Fisica Applicata “Nello Carrara”, Consiglio Nazionale delle Ricerche (CNR), Sesto Fiorentino, Italy, 3 Museo Storico della Fisica e Centro Studi e Ricerche Enrico Fermi, Roma, Italy, 4 Instituto de Catálisis y Petroleoquímica, Consejo Superior de Investigaciones Científicas (CSIC), Madrid, Spain
منابع مشابه
Spectroscopy and 1μm Luminescence by Visible Quantum Cutting in Pr3+-Yb3+ Codoped Glass
The quantum cutting phenomenon of a blue photon into two infrared photons is reported in glass codoped with Pr-Yb ions. Oxyfluoride glass with compositions of 32SrF2-0.1PrF3-2.9YbF3-42SiO2-23Al2O3 were prepared, and photoluminescence properties in the range from visible to near-infrared were investigated. Evidence of several energy transfers, such as (Pr:P0→G4)→(Yb:F5/2←F7/2) and (Pr:D2→F4, F3)...
متن کاملUpconversion luminescence in Er-doped germanate-oxyfluoride and tellurium-germanate-oxyfluoride transparent glass-ceramics
Upconversion luminescence has been studied for Er in a germanate-oxyfluoride and a tellurium-germanate-oxyfluoride transparent glass-ceramic using 800 nm excitation. Significantly increased upconversion luminescence was observed from transparent glass-ceramics compared with that from their corresponding as-prepared glasses. In addition to a strong green emission centered at 545 nm from S3/2 sta...
متن کاملLuminescence Properties of Oxyfluoride Glass and Glass Ceramic Doped with Y3 + Ions
Oxyfluoride glass ceramics containing CaF2nano-crystals doped with Y3+ ions were prepared by one-step crystallization of SiO2- Al2O3- CaO- CaF2 glasses at different temperatures. X- ray diffraction (XRD) results have revealed that CaF2 was the only precipitated crystalline phase in glass ceramic samples. According to the XRD results, a glass ceramic was selected as the best sample in order to ...
متن کاملDistribution of Nd3+ ions in oxyfluoride glass ceramics
It has been an open question whether Nd3+ ions are incorporated into the crystalline phase in oxyfluoride glass ceramics or not. Moreover, relative research has indicated that spectra characters display minor differences between before and after heat treatment in oxyfluoride glass compared to similar Er3+-, Yb3+-, Tm3+-, Eu3+-, etc.-doped materials. Here, we have studied the distribution of Nd3...
متن کاملThe Crystallization Effect on the Optical Properties of Oxyfluoride Glass-Ceramics Containing CaF2 Nanocrystals Doped with Y3+ Ions
In the present study, the oxyfluoride glasses of SiO2-Al2O3-CaF2 system containing different amounts of Y3+ ions were prepared through the convenient melting method. The crystallization temperatures and size of the CaF2 nanocrystals were obtained from DTA curves and XRD patterns, respectively. As a consequence, the optimum amount...
متن کامل