DESCRIPTION OF STRUCTURE OF Fe-Zn INTERMETALIC COMPOUNDS PRESENT IN HOT-DIP GALVANIZED COATINGS ON STEEL
نویسندگان
چکیده
P. Pokorny, J. Kolisko, L. Balik – Czech Technical University – Klokner Institute, Prague, Czech Republic P. Novak – Institute of Chemical Technology, Prague, Czech Republic The article is describing formation, composition, morphology and crystallographic characteristics of intermetalic compounds Fe Zn present in the coating formed during the process of low-temperature hot-dip galvanizing of carbon steels. In mutual confrontation we introduce older bibliography and results of latest modern researches based on combination of most precise analytical methods.
منابع مشابه
Formation oF outburst struCturE in hot dip galvannEalEd Coatings on iF stEEls
Rapid development of automotive industry brings also increased requirements for sheets properties, involving relatively high strength and good formability together with excellent corrosion resistance. Increasing requests for corrosion resistance lead to the production of coated car parts, protected mainly by zinc coatings. Whereas, majority of European producers of passenger cars use preferenti...
متن کاملOptimization of exposure time for hot dip galvanizing and study the effects of preflux bath additives on the microstructures of galvanized steel
The objective of this research work is to optimize the time of exposure for hot dip galvanizing of mild steel, so as to achieve such a microstructure of zinc coating that protects mild steel for long against atmospheric corrosion. In order to decide the above mentioned parameter the polished samples, one at a time, were dipped in to 500 g molten zinc at 460 to 470 oC in the crucible for a diffe...
متن کاملEffect of Aluminum on Microstructure and Thickness of Galvanized Layers on Low Carbon silicon-Free Steel
In hot dip galvanizing, several parameters such as chemical composition of coating bath, immersion time and surface roughness of specimens could affect microstructure and properties of coating. In this article, the effect of aluminum content, immersion time and surface roughness on structure and properties of alloy layers have been investigated. Specimens of low carbon silicon-free steel with d...
متن کاملREACTION KINETICS OF THE FORMATION OF INTERMETALLIC Fe – Zn DURING HOT - DIP GALVANIZING OF STEEL
P. Pokorny, J. Kolisko, L. Balik – Czech Technical University – Klokner Institute, Prague, Czech Republic P. Novak – Institute of Chemical Technology, Prague, Czech Republic This review article mainly describes the composition of intermetallic Fe Zn, i.e. zeta (ζ), delta (δ1k + δ1p), gamma1 (Γ1) and gamma (Γ) on galvanized steel during low temperature galvanization (t ~ 450 °C). It gives detail...
متن کاملEffect of Mg on the Microstructure and Corrosion Resistance of the Continuously Hot-Dip Galvanizing Zn-Mg Coating
The microstructure of continuously hot-dip galvanizing Zn-Mg coating was investigated in order to obtain the mechanism of the effects of Mg on the corrosion resistance. In this paper, the vertical section of the Zn-0.20 wt % Al-Mg ternary phase diagram near the Al-low corner was calculated. The results indicates that the phase composition of the Zn-0.20 wt % Al-Mg ternary phase diagram near the...