Synthesis and characterization of mesoporous silica core-shell particles
نویسندگان
چکیده
Core-shell particles were formed by deposition of primary silica particles synthesized from sodium silicate solution on functionalized silica core particles (having size of ~0.5 μm) prepared by hydrolysis and condensation of tetraethylortosilicate. The obtained mesoporous shell has thickness of about 60 nm and consists of primary silica particles with average size of ~21 nm. Scanning electron microscopy and zeta potential measurements showed that continuous silica shell exists around functionalized core particles which was additionally proved by FTIR and TEM results
منابع مشابه
Preparation and Characterization of Double Shell Fe3O4 Cluster@Nonporous SiO2@Mesoporous SiO2 Nanocomposite Spheres and Investigation of their In Vitro Biocompatibility
Background: Multifunctional core-shell magnetic nanocomposite particles with tunable characteristics have been paid much attention for biomedical applications in recent years. A rational design and suitable preparation method must be employed to be able to exploit attractive properties of magnetic nanocomposite particles. Objectives: Herein, we report on a simple approach for the synthesis of m...
متن کاملSurfactant Removal from Mesoporous Silica Shell of Core-Shell Magnetic Microspheres by Modified Supercritical CO2
In this paper, a kind of core–shell magnetic mesoporous microspheres of Fe3O4@SiO2@meso-SiO2 with high surface areawas prepared, where magnetic Fe3O4 nanospheres were used as the inner core, tetraethyl orthosilicate (TEOS) as silica source, and cetyltrimethylamonium bromide (CTAB) as pore forming agent. Methanol-enhanced s...
متن کاملSynthesize and Characterization of Mesoporous ZrFe2O4@SiO₂ Core-shell Nanocomposite Modified with APTES and TCPP
The mesoporous ZrFe2O4 nanocauliflowers were synthesized via the solvothermal method. The core-shell ZrFe2O4@SiO2 nanocomposite was successfully prepared by a simple wet route using tetraethylorthosilicate, then modified with (3-aminopropyl)triethoxisilan (APTES) as link...
متن کاملSynthesis and characterization of CdS nanoparticle anchored Silica-Titania mixed Oxide mesoporous particles: Efficient photocatalyst for discoloration of textile effluent
An efficient photocatalyst consisting of CdS nanoparticle dispersed mesoporous silica-titania was prepared using amphiphilic triblock copolymer P123 as template and silica-titania sol–gel precursors. The CdS nanoparticle was incorporated into silica-titania mesoporous nanosturctures by post impregnation method. The synthesized catalyst has been characterized by FTIR, TEM, SEM, and EDAX analysis...
متن کاملMulti-step Coating of Monodisperse Silica Spheres by Titania Nanoparticles Base on Electrostatic Attraction Strategy
TiO2-SiO2 core-shell particles include of monodisperse silica core and nanostructured titania shell were synthesized by a multi-step coating process. The monodisperse silica spheres were synthesized by Stöber method and titania shell was obtained of a colloidal sol prepared by a hydrolysis–condensation reaction. The titania sol was deposited on monodisperse silica spheres by a multi-step coatin...
متن کامل