Evidence of dislocation cross-slip in MAX phase deformed at high temperature
نویسندگان
چکیده
Ti₂AlN nanolayered ternary alloy has been plastically deformed under confining pressure at 900°C. The dislocation configurations of the deformed material have been analyzed by transmission electron microscopy. The results show a drastic evolution compared to the dislocation configurations observed in the Ti₂AlN samples deformed at room temperature. In particular, they evidence out-of-basal-plane dislocations and interactions. Moreover numerous cross-slip events from basal plane to prismatic or pyramidal planes are observed. These original results are discussed in the context of the Brittle-to-Ductile Transition of the nanolayered ternary alloys.
منابع مشابه
Plasticity mechanisms in HfN at elevated and room temperature
HfN specimens deformed via four-point bend tests at room temperature and at 2300 °C (~0.7 Tm) showed increased plasticity response with temperature. Dynamic diffraction via transmission electron microscopy (TEM) revealed ⟨110⟩{111} as the primary slip system in both temperature regimes and ⟨110⟩{110} to be a secondary slip system activated at elevated temperature. Dislocation line lengths chang...
متن کاملDISLOCATIONS STRUCTURE AND SCATTERING PHENOMENON IN CRYSTALLINE CELL SIZE OF 2024 AL ALLOY DEFORMED BY ONE PASS OF ECAP AT ROOM TEMPERATURE
Variation in microstructural features of 2024 aluminum alloy plastically deformed by equal channel angular pressing (ECAP) at room temperature, was investigated by X-Ray diffraction in this work. These include dislocation density dislocation characteristic and the cell size of crystalline domains. Dislocations contrast factor was calculated using elastic constants of the alloy such as C 11, C 2...
متن کاملSmall-Angle Neutron Scattering Study of Dislocations in Deformed Single-Crystal Copper
Small-angle neutron scattering measurements of deformed single-crystal copper have been performed over a wave-vector transfer range of 0.0655 <__ Q < 1.32 nm l . The measurements included four samples deformed in compression at room temperature along the [110] direction to 6.8, 15.6, 35.0 and 54.3% reduction in thickness and an undeformed reference sample. The response of the reference sample f...
متن کاملINTERNAL FRICTION OF DEFORMED NaCL
Internal friction of deformed oriented NaCl single crystals has been measured as a function of flow stress, strain amplitude, frequency, temperature and divalent doping. In pure NaCl af er deformation a maximum of internal friction PI is observed at low temperatures. With increasing 1+ Sr doping a second but much weaker peak P2 appears at higher temperatures. The dependencies of PI on the...
متن کاملThrough-Focal HAADF-STEM Analysis of Dislocation Cores in a High-Entropy Alloy
High-entropy alloys (HEAs) are a new class of multi-component alloys that exhibit surprising characteristics, [1] including very large strain hardening rates, large fracture toughness at room temperature [2], and a strong temperature dependence of yield strength at or below room temperature. These properties are closely linked to nano-twinning and dislocation-mediated plasticity, yet little exp...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره 4 شماره
صفحات -
تاریخ انتشار 2014