Use of heat of adsorption to quantify amorphous content in milled pharmaceutical powders.

نویسندگان

  • Shamsul Alam
  • Mahmoud Omar
  • Simon Gaisford
چکیده

Isothermal calorimetry operated in gas perfusion mode (IGPC) is often used to quantify the amorphous content of pharmaceutical powders. Typically, the calibration line is constructed using the heat of crystallisation as the sample is exposed to high levels of a plasticising vapour. However, since the physical form to which the amorphous fraction crystallises may be dependent on the presence of any crystalline seed, the calibration line is often seen to be non-linear, especially as the amorphous content of the sample approaches 100% w/w. Redesigning the experiment so that the calibration line is constructed with the heat of adsorption is an alternative approach that, because it is not dependent upon crystallisation to a physical form should ameliorate this problem. The two methods are compared for a model compound, salbutamol sulphate, which forms either a hydrate or an anhydrate depending on the amorphous content. The heat of adsorption method was linear between amorphous contents of 0 and 100% w/w and resulted in a detection limit of 0.3% w/w and a quantification limit of 0.92% w/w. The heat of crystallisation method was linear only between amorphous contents of 0 and 80% w/w and resulted in a detection limit of 1.7% w/w and a quantification limit of 5.28% w/w. Thus, the use of heat of adsorption is shown to be a better method for quantifying amorphous contents to better than 1% w/w.

برای دانلود رایگان متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Mechanisms and quantification of disorder

Pazesh, S. 2017. Process-induced disorder of pharmacutical materials. Mechanisms and quantification of disorder. Digital Comprehensive Summaries of Uppsala Dissertations from the Faculty of Pharmacy 69 pp. : 1. ISBN 978-91-554-9860-3. One of the most important prerequisites in the drug development is to attain a reproducible and robust product in terms of its nature, and its chemical and physic...

متن کامل

بررسی تغییرات فازی سیلیس و سیلیسیوم به هنگام آسیاب کاری

In the present study phase transformation of silicon and silica during milling in different atmospheres was investigated. The silicon powder was subjected to high energy ball milling in ammonia (25%) atmosphere. The milled powder was subsequently annealed at 1200 ◦C for 1 hour. In another test a mixture of AlN and amorphous silica (micro silica) was subjected to high energy ball milling. The m...

متن کامل

Effect of Amorphous Silica Addition on Martensitic Phase Transformation of Zirconia and Investigation of its Tetragonal Structure Stability Mechanisms

This work is focused on the effect of amorphous SiO2 addition on the phase transformation and microstructural evolution of ZrO2 particles. Considering the structural similarities between the amorphous ZrO2 and its tetragonal structure, XRD results showed initial nucleation of metastable tetragonal ZrO2 from its amorphous matrix upon heat treatment. This metastable phase is unstable in pure ZrO2...

متن کامل

Effect of Chromium Content on Formation of (Mo1-x-Crx) Si2 Nanocomposite Powders via Mechanical Alloying

(Mo1-x-Crx)Si2 composite powders were successfully synthesized by ball milling of Mo, Cr and Si elemental powders. Effects of the Cr content, milling time and annealing temperature were investigated. X-ray diffraction (XRD) was used to characterize the milled and annealed powders. The morphological and microstructural evolutions were studied by scanning electron microscopy (SEM) and transmissio...

متن کامل

Mechanochemical synthesis of alumina nanoparticles

Abstract: Nano- size alumina particles have been synthesized by mechanical activation of a dry powder mixture of AlCl3 and CaO. Mechanical milling of the above raw materials with the conditions adopted in this study resulted in the formation of a mixture consisting of crystalline CaO and amorphous aluminum chlorides phases. There was no sign of chemical reaction occurring during milling stag...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

عنوان ژورنال:
  • International journal of pharmaceutics

دوره 459 1-2  شماره 

صفحات  -

تاریخ انتشار 2014