Microstructure, optical properties, and catalytic performance of Cu2O-modified ZnO nanorods prepared by electrodeposition
نویسندگان
چکیده
Cu2O-modified ZnO nanorods are prepared by a two-step electrodeposition method on ITO substrates, and the deposition time of Cu2O is 0, 1, 5, and 10 min, respectively. Cu2O particles are embedded in the interspaces of the ZnO nanorods, and the amounts of the Cu2O particles increase obviously when the deposition time lasts longer. The peaks corresponding to ZnO nanorods and Cu2O particles are detected from scanning electron microscope (SEM) and X-ray diffraction (XRD) results. UV-vis absorption spectra measurements have shown the bandgaps of ZnO nanorods shift from 3.22 to 2.75 eV. The methyl orange (MO) concentration can be reduced to around 15% in 100 min with Cu2O electrodeposition time for 10 min.
منابع مشابه
Changing the thickness of two layers: i-ZnO nanorods, p-Cu2O and its influence on the carriers transport mechanism of the p-Cu2O/i-ZnO nanorods/n-IGZO heterojunction
In this study, two layers: i-ZnO nanorods and p-Cu2O were fabricated by electrochemical deposition. The fabricating process was the initial formation of ZnO nanorods layer on the n-IGZO thin film which was prepared by sputtering method, then a p-Cu2O layer was deposited on top of rods to form the p-Cu2O/i-ZnO nanorods/n-ZnO heterojunction. The XRD, SEM, UV-VIS, I-V characteristics methods were ...
متن کاملInfluence of Cr dopant on the microstructure and optical properties of ZnO nanorods
One-dimensional (1D) undoped and Cr doped ZnO nanorods with average length of 1 µm and diameter of 80 nm were synthesized using hydrothermal method where a fast growth of ZnO nanorods on the seed layer was observed. Afterwards, the effects of Cr dopant on structural, surface morphology and optical properties of nanorods were studied using X-ray diffraction (XRD), scanning electron microscopy (S...
متن کاملElectronic Structure Engineering of Cu2O Film/ZnO Nanorods Array All-Oxide p-n Heterostructure for Enhanced Photoelectrochemical Property and Self-powered Biosensing Application
We have engineered the electronic structure at the interface between Cu2O and ZnO nanorods (NRs) array, through adjusting the carrier concentration of Cu2O. The electrodeposition of Cu2O at pH 11 acquired the highest carrier concentration, resulting in the largest interfacial electric field between Cu2O and ZnO, which finally led to the highest separation efficiency of photogenerated charge car...
متن کاملDimethylamine Controlled Sol-Gel Process to Grow ZnO Nanorods
ZnO nanorods were prepared using dimethylamine (DMA) controlled Sol-Gel process. Dimethylamine was added as an additive to control the sol-gel process for growing ZnO nanorods. DMA would exhibit stabilizing effect, promote dissolution of precursor and control the rate of sol-gel reactions because of its basic nature and significant miscibility. The Structural and microstructural properties of t...
متن کاملMicrostructure and optical properties of nanocrystalline Cu2O thin films prepared by electrodeposition
Cuprous oxide (Cu2O) thin films were prepared by using electrodeposition technique at different applied potentials (-0.1, -0.3, -0.5, -0.7, and -0.9 V) and were annealed in vacuum at a temperature of 100°C for 1 h. Microstructure and optical properties of these films have been investigated by X-ray diffractometer (XRD), field-emission scanning electron microscope (SEM), UV-visible (vis) spectro...