Microshear bond strength according to dentin cleansing methods before recementation

PURPOSE THE AIM OF THIS STUDY WAS TO DETERMINE THE EFFICIENCY OF ERBIUM, CHROMIUM: Yttrium-Scandium-Gallium-Garnet laser in different output powers for removing permanent resin cement residues and therefore its influence on microshear bond strength compared to other cleaning methods. MATERIALS AND METHODS 90 extracted human molars were sectioned in 1 mm thickness. Resin cement was applied to surface of sliced teeth. After the removal of initial cement, 6 test groups were prepared by various dentin surface treatment methods as follows: no treatment (Group 1), ethylene diamine tetra acetic acid application (Group 2), Endosolv R application (Group 3), 1.25 W Erbium, Chromium:Yttrium-Scandium-Gallium-Garnet laser irradiation (Group 4), 2 W Erbium, Chromium:Yttrium-Scandium-Gallium-Garnet laser irradiation (Group 5) and 3.5 W Erbium, Chromium:Yttrium-Scandium-Gallium-Garnet laser irradiation (Group 6). The topography and morphology of the treated dentin surfaces were investigated by scanning electron microscopy (n=2 for each group). Following the repetitive cementation, microshear bond strength between dentin and cement (n=26 in per group) were measured with universal testing machine and the data were analyzed by Kruskal Wallis H Test with Bonferroni correction (P<.05). Fracture patterns were investigated by light microscope. RESULTS Mean microshear bond strength ± SD (MPa) for each group was 34.9 ± 17.7, 32.1 ± 15.8, 37.8 ± 19.3, 31.3 ± 12.7, 44.4 ± 13.6, 40.2 ± 13.2 respectively. Group 5 showed significantly difference from Group 1, Group 2 and Group 4. Also, Group 6 was found statistically different from Group 4. CONCLUSION 2 W and 3.5 W Erbium, Chromium: Yttrium-Scandium-Gallium-Garnet laser application were found efficient in removing resin residues.