Dry Sliding Wear Behavior of Ti6Al4V and TaN against TiN Deposited Steel Surface
نویسندگان
چکیده
The objective of this research is to study the dry sliding wear behaviour of metal surfaces and influences of their surface hardness. The improved hardness of the TiN deposited surface was about 1763 Hv. The worn surface Scanning Electron Microscope (SEM) morphology exhibits the surface damage due to varying wear test parameters. The Electron Dispersive Spectroscopy (EDS) reveals that the material transfer between the counter parts and the wear mechanism has been involved. The minimum specific wear rate of TiN surface was 0.0018 mg/Nm and 0.0026 mg/Nm against Ti6Al4V alloy and TaN respectively.
منابع مشابه
Wear and frictional mechanisms of copper-based bearing alloys
The present study investigated the role of alloy microstructure and surface roughness on wear and friction behavior of leaded and unleaded tin bronzes. Ball-on-disk experiments were carried out under dry conditions with steel balls sliding against bronze disks. Scanning electron microscopy (SEM), energy dispersive electron microscopy (EDX), x-ray photoelectron spectroscopy (XPS) and Auger elect...
متن کاملCOMPARISON OF THE CrN , TiN AND (Ti, Cr)N PVD COATINGS DEPOSITED BY CATHODIC ARC EVAPORATION
In the present study, CrN, TiN and (Ti, Cr)N coatings were deposited on D6 tool steel substrates. Physical and mechanical properties of coatings such as microstructure, thickness, phase composition, and hardness were evaluated. Phase compositions were studies by X-ray diffraction method. Mechanical properties were determined by nano-indentation technique. The friction and wear behaviour of the ...
متن کاملFriction and Wear Behaviors of Gear Steel under Coupling of Rolling and Sliding
In this paper, the gear material 20CrMnTi was selected as the research object. Friction and wear behavior was performed on the M2000 friction and abrasion tester. The friction and wear mechanisms of 20CrMnTi steel were discussed under coupling of rolling and sliding. The results show that damage of steel-steel couples under coupling of rolling and sliding is caused by the interaction of mechani...
متن کاملSelf-Cleaning Properties of TiN/CrN Nanoscale Multi-layer Deposited on Surgical 420C Stainless Steel
The present paper focuses on the investigation of self-cleaning properties based on studding of water repellency and blood repellency for TiN- and CrN single-layer and TiN/CrN nanoscale multi-layer coatings deposited via Cathodic Arc Evaporation (CAE) method on medical grade 420C stainless steel substrate. X-ray diffraction (XRD) method and Field Emission Scanning Electron Microscope (FESEM) wa...
متن کاملEnhancement Wear Properties of HSS-M2 Tool Steel with WC Deposited by SMAW Process
In this study, the effect of cladded tungsten carbide layer upon HSS - M2 tool steel on microstructure, hardness, and wear behavior has been studied in two cases without using the middle layer and using the middle layer of nickel. Tungsten Carbide cladded on HSS - M2 tool steel by Arc Weld ( SMAW ). The ASTM-G65 wear test was used to determine its application for use in the mineral indus...
متن کامل