Surface Coatings of TiO2 Nanoparticles onto the Designed Fabrics for Enhanced Self-Cleaning Properties
نویسندگان
چکیده
Herein, the hydrophobic and self-cleaning properties of three different fabric surfaces have been evaluated after applying titanium dioxide (TiO2) nanofinishes. The nanoparticles were prepared by sol-gel techniques and were characterized by using X-ray diffraction (XRD), scanning electron microscopy (SEM) and dynamic light scattering (DLS) methods. The ultra-refined particles were applied over three different fabric substrates having similar weave of Z-twill (3/1). The yarns of 100% polyester, blend of viscose with mod-acrylic and high performance polyethylene containing 16 yarn count (Ne) and 31.496 and 15.748 ends/cm and picks/cm, respectively, were used for required fabric preparation. The different fabric structures were applied with self-cleaning finish of TiO2 nanoparticles prepared in our laboratory and the results were compared with commercially available finish Rucoguard AFR. The static contact angles, UV-protection factor, air permeability and hydrophobic activity of nanofinished fabric helped in evaluating their breathability and self-cleaning properties.
منابع مشابه
The effect of Inorganic Nanoparticles on Camouflage Properties of Cotton/Polyester Fabrics
Drawing upon reflectance behavior of woodland colors involving dark brown in the UV-Vis-IR bands, two colored pigments were used to print cotton/polyester Co/PET goods. Inorganic nanoparticles of TiO2, ZnO and AL2O3 were also loaded onto the printing formulation. The reflectance profile of treated samples was studied using Jasco V-670 reflectance spectrophotometer. SEM analysis of printed fabri...
متن کاملPhotocatalytic self-cleaning properties of lanthanum and silver co-doped TiO2 nanocomposite on polymeric fibers
Titania, single-doped and lanthanum-silver co-doped titania nanocomposite were coated on cellulosic and polyacrylonitrile fibers via sol–gel method. The prepared samples were evaluated using x-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive x-ray spectroscopy (EDX), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), photolumines...
متن کاملPhotocatalytic self-cleaning properties of lanthanum and silver co-doped TiO2 nanocomposite on polymeric fibers
Titania, single-doped and lanthanum-silver co-doped titania nanocomposite were coated on cellulosic and polyacrylonitrile fibers via sol–gel method. The prepared samples were evaluated using x-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive x-ray spectroscopy (EDX), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), photolumines...
متن کاملAdsorption and Photocatalytic Properties of Surface-Modified TiO2 nanoparticles for Methyl Orange Removal from Aqueous Solutions
Titanium dioxide nanoparticles surface-modified by 5-sulfosalicylic acid 5-SA-TiO2 were prepared in ethanol by the chemisorption process. The effects of surface improvement on the photocatalytic degradation and adsorption of methyl orange MO were studied in a batch system by considering the various parameters, such as contact time, adsorbent dosage, pH, initial dye concentration and temperature...
متن کاملUV protection and self-cleaning finish for cotton fabric using metal oxide nanoparticles
Ultra-violet protection and self-cleaning action of nano zinc oxide (ZnO) and titanium di-oxide (TiO2) with acrylic binder has been assessed on the cotton fabric using pad-dry-cure method. Different precursors, such as zinc acetate and titanium tetrachloride have been used to synthesize nanoparticles. Zinc acetate is synthesized into nanoparticle by wet chemical technique and titanium tetrachlo...
متن کامل