The Nature, Mechanism and Properties of Strong Bainite
نویسنده
چکیده
: Consistent with the wishes of the Conference Organisers, the basic theory of the bainite reaction including the crystallographic, thermodynamic and kinetic framework is described, together with the development of fine bainite and its properties.
منابع مشابه
Mechanism of Bainite Transformation in Fe-Cr-Mo-V-Ti-C Steel
The kinetics and mechanism of bainite transformation have been studied in Fe-Cr-Mo-V-Ti-C steel high speed dilatometry backed by thermodynamic analysis. The complete transformation of austenite, however, has not occurred at any reported temperature. Obtained results confirm the incomplete reaction phenomenon with the cessation of the bainite transformation well before the paraequilibrium is ach...
متن کاملStudy of the effects of lower bainite volume fraction on tensile and impact properties of D6AC medium carbon low alloy ultrahigh strength steel
The effects of lower bainite volume fraction on tensile and impact properties of D6AC ultrahigh strength steel were studied in the current work. To obtain mixed microstructures containing martensite and different volume fractions of the lower bainite, specimens were austenitized at 910° C, then quenched in a salt bath of 330°C for different holding times, finally quenched in oil. In order to ob...
متن کاملVery strong low temperature bainite
Bainite has been obtained by heat treatment at temperatures as low as 125°C in a high carbon, high silicon steel. This has had the effect of greatly re® ning the microstructure, which is found to have a strength in excess of 2.5 GPa together with an ability to ̄ ow plastically before fracture. Such properties have never before been achieved with bainite. In this paper metallographic details are ...
متن کاملVery Strong, Low–Temperature Bainite
During the course of our research on the quantitative design of steels [1,2], an exciting discovery was made, in which carbide–free bainite was obtained by transformation at incredibly low temperatures, as low as 125 ◦C [3]. To put this into context, the random jump distance of an iron atom at that temperature is only 10 m over a period of three weeks. The consequence of the low transformation–...
متن کاملInfluence of carbon, manganese and nickel on microstructure and properties of strong steel weld metals Part 2 – Impact toughness gain resulting from manganese reductions
Two experimental high strength steel weld metals were produced with 7 wt-% nickel and either 2 or 0.5 wt-% manganese. Neural network predictions that it is advantageous to reduce the manganese concentration in high nickel alloys have been confirmed, with impact energy increasing from 32 to 113 J at –40uC. High resolution microstructural investigations showed that both weld metals contained main...