Effect of the Homogenizing Treatment on the Properties of High Magnetic Permeability
نویسنده
چکیده
900°C for 1hr after melting in air. These high permeability alloys have been named "Nimalloy." It is not considered, however, that the alloys are sufficiently homogenized by these treatments since a large discrepancy between the solidus and liquidus lines in the Ni-Mn system may result in tremendous segregation of the alloys on solidifying. Therefore, homogenization and purification of the alloys are made at temperatures above 900°C, and then the magnetic
منابع مشابه
Effect of Heat Treatment on Microstructure, Magnetic and Mechanical Properties of HSLA-100
In this study, the effects of various heat treatments on microstructure, mechanical and magnetic properties of HSLA-100 steel were evaluated. The heat treatments consisted of austenitizing at 900°C for 60 minutes, then quenching by different cooling rates via furnace, air, oil and water; and quenched specimens were aged at 600°C for one hour. Optical and field emission scanning electron m...
متن کاملThe Effect of Heat Treatment on Microstructure and Magnetic Properties of Nd17Fe76.5B5Cu1.5 Type Sintered Magnets
The effects of high temperature homogenization and low temperature annealing treatments on the microstructure and magnetic properties of sintered magnets of an Nd17Fe76.5B5Cu1.5 type alloy have been investigated. The microstructure of the as-cast alloy, consisted of three phases including a Nd2Fe14B1 (2:14:1- type) matrix phase Cu-containing Nd-rich Phase and Free α-iron. The as-sintered magnet...
متن کاملThe Effect of Heat Treatment on Microstructure and Magnetic Properties of Nd17Fe76.5B5Cu1.5 Type Sintered Magnets
The effects of high temperature homogenization and low temperature annealing treatments on the microstructure and magnetic properties of sintered magnets of an Nd17Fe76.5B5Cu1.5 type alloy have been investigated. The microstructure of the as-cast alloy, consisted of three phases including a Nd2Fe14B1 (2:14:1- type) matrix phase Cu-containing Nd-rich Phase and Free α-iron. The as-sintered magnet...
متن کاملAn Experimental Investigation of Magnetized Water Effect on Formation Damage
In oil industries, water injection into oil reservoirs for pressure maintenance, oil displacement, and oil recovery is a common technique. Formation damage during water injection is a major problem in this process. Formation damage from the incompatibility of formation water (FW) and injection water (IW) causes a reduction in the permeability around the injection wells. Therefore, it is necessa...
متن کاملMagnetic and Electrical Properties of Nanocrystalline Fe85Si10Ni5/Phenolic Resin Soft Magnetic Composites
In this work, nanocrystalline Fe85Si10Ni5 soft magnetic powders were prepared by mechanical alloying and subsequent annealing to reduce the internal stresses and lattice strains. The powders were mixed with phenolic resin and warm pressed to produce nanostructured soft magnetic composites. The effect of annealing time and temperature on the crystalline structure, microstructure and magnetic pro...
متن کامل