Cobalt doped Zinc ferrites, CoxZn1-xFe2O4, (x = 0, 0.2, 0.4, and 0.6) were prepared by chemical solution method using metallo-organic precursors. The crystalline structure, microstructure, magnetic and dielectric properties of the samples were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), vibrating sample magnetometer (VSM) and impedance analyser respectively. All samples show cubic spinel structure with minor Fe2O3 phase and lattice parameter decreases from 8.419Å to 8.308Å with increasing cobalt content from 0 to 60%. Magnetic measurement shows that CoxZn1-xFe2O4 samples exhibit ferromagnetic behavior at room temperature. The saturation magnetization initially increases from 2.17 to 71.2emu/g on increasing Co content to 40% and then decreases to value 55.9emu/g at Co concentration of 60%. The coercivity also increases to Hc ~ 330Oe for the sample with Co=20% and then decreases to minimum value of Hc ~ 32Oe for sample having 40% Co content. The coercivity value is then increases and is measured as Hc ~ 154Oe for sample with 60% Co content. The magnetic properties are explained in terms of cation distribution and grain size effect. The dielectric properties of the samples were studied with varying temperature and frequencies. The dielectric properties are influenced by electron hopping mechanism between Fe and Fe ions.
منابع مشابه
Synthesis of Different Copper Oxide Nano-Structures From Direct Thermal Decomposition of Porous Copper(ΙΙ) Metal-Organic Framework Precursors
Copper oxide nanostructures have been successfully synthesized via one-step solid-state thermolysis of two metal-organic frameworks, [Cu3(btc)2] (1) and [Cu(tpa).(dmf)] (2), (btc = benzene-1,3,5-tricarboxylate, tpa = therephtalic acid = 1,4-benzendicarboxylic acid and dmf = dimethyl formamide) under air atmosphere at 400, 500, and 600°C. It has also been found that the reaction temperature pla...
متن کاملCatalytic Decomposition of H2O2 on MnFe2O4 Nanocomposites Synthesized by Various Methods in the Presence of Silicate and Zeolite Supports
In this research iron manganese oxide nanocomposites were prepared by co-precipitation, sol-gel and mechanochemical methods by using iron (III) nitrate, iron (II) sulfate and manganese (II) nitrate as starting materials. These nanocomposites were prepared in the presence of various catalyst beds. The polyvinyl pyrrolidon (PVP) was used as a capping agent to control the agglomeration of the nano...
متن کاملCatalytic Decomposition of H2O2 on MnFe2O4 Nanocomposites Synthesized by Various Methods in the Presence of Silicate and Zeolite Supports
In this research iron manganese oxide nanocomposites were prepared by co-precipitation, sol-gel and mechanochemical methods by using iron (III) nitrate, iron (II) sulfate and manganese (II) nitrate as starting materials. These nanocomposites were prepared in the presence of various catalyst beds. The polyvinyl pyrrolidon (PVP) was used as a capping agent to control the agglomeration of the nano...
متن کاملIn this paper, the effect of nanocatalytic metal-organic framework based on copper metal and bis-tetrazolamine (CuBTA) ligand functionalized with cobalt (II) oxide nanoparticles on the thermal decomposition behavior of ammonium perchlorate (AP), using differential survey calorimetry (DSC) has been reviewed. First, the metal-organic framework (CuBTA) was synthesized from the raw materials of cop...
متن کاملCobalt oxide nanoparticles by solid-state thermal decomposition: Synthesis and characterization
In this study, mononuclear octahedral cobalt(III) Schiff base complex [CoL3], L = (5-bromo-2-hydroxybenzyl-2-furylmethyl)imine, was synthesized from the reaction of Co(NO3)2•6H2O and the Schiff base ligand L in methanol as solvent. It used as a new precursor to prepare spinel type cobalt oxide nanoparticles by a facile solid-state thermal decomposition. Controlling the temperature and time, Co3...
متن کامل