Enhancing Protein Incorporation in Calcium Phosphate Coating on Titanium by Rapid Biomimetic Co-Precipitation Technique
نویسندگان
چکیده
Calcium phosphate coating (CaP) has been employed for protein delivery, but the typical direct protein adsorption on the coating led to low incorporation content and fast release of the protein from the coating. By using bovine serum albumin (BSA) as a model protein, rapid biomimetic co-precipitation between calcium phosphate and BSA was employed to control the distribution of BSA within calcium phosphate coating during biomimetic formation on titanium surface for only 6 h at 50C in an accelerated calcium phosphate solution. As a result, the amount of BSA incorporation and release duration could be increased by using a rapid biomimetic coprecipitation technique. Up to 43 fold increases in the BSA incorporation content and the increase from 6 h to more than 360 h in release duration compared to typical direct adsorption technique were observed depending on the initial BSA concentration used during coprecipitation (1, 10 and 100 μgml). From x-ray diffraction and Fourier transform infrared spectroscopy studies, the coating composition was not altered with the incorporation of BSA by this rapid biomimetic co-precipitation and mainly comprised octacalcium phosphate and hydroxyapatite. However, the microstructure of calcium phosphate crystals changed from straight, plate-like units to curved, plate-like units with increasing BSA content. Keywords—Biomimetic, Calcium Phosphate Coating, Protein, Titanium.
منابع مشابه
In vitro study on the osteogenesis enhancement effect of BMP-2 incorporated biomimetic apatite coating on titanium surfaces.
To fabricate a sustained-release delivery system of bone morphogenetic protein (BMP-2) on titanium surface, explore the effect of BMP-2 concentration on the loading/release behavior of BMP-2 and evaluate the cell compatibility of the system in vitro, pure titanium specimens were immersed into supersaturated calcium phosphate solutions (SCP) containing 4 different concentrations of BMP-2: 0, 50,...
متن کاملBiomimetic Hydroxyapatite Coating on Metal Implants
The combination of the high mechanical strength of metals with the osteoconductive properties of calcium phosphates make hydroxyapatite coatings on titanium implants widely used in orthopedic surgery. However, the most popular coating method, plasma spraying, exhibits some important drawbacks: the inability to cover porous implants and to incorporate biologically active agents, delamination, an...
متن کاملEffect of Alkaline-Acid Treatment on the Biomimetic Formation of Calcium Phosphate Layers on Titanium Substrates:An In Vitro Study
متن کامل
Hybrid calcium phosphate coatings with the addition of trace elements and polyaspartic acid by a low-thermal process.
Research in the field of orthopedic implantology is currently focused on developing methodologies to potentiate osseointegration and to expedite the reestablishment of full functionality. We have developed a simple biomimetic approach for preparing trace elements-codoped calcium phosphate (teCaP) coatings on a titanium substrate. The reaction proceeded via low-thermal incubation in trace elemen...
متن کاملEffect of pulsed current densities on co-electrodeposition of Graphene Oxide/ Calcium-Phosphate coatings and their biocompatibility
In this study, calcium-phosphate (Ca-P) and graphene oxide (GO)/ calcium-phosphate (Ca-P) coatings were electrodeposited with different pulsed current densities on TiO2 nanotubes. Results showed that the co-electrodeposition rate in the presence of GO, especially at low current densities of 2 and 5 mA/cm2, significantly decreased. This might be due to the large size of GO sheets as compared to ...
متن کامل