Magnetoresistance in Sn-Doped In2O3Nanowires
نویسندگان
چکیده
In this work, we present transport measurements of individual Sn-doped In2O3nanowires as a function of temperature and magnetic field. The results showed a localized character of the resistivity at low temperatures as evidenced by the presence of a negative temperature coefficient resistance in temperatures lower than 77 K. The weak localization was pointed as the mechanism responsible by the negative temperature coefficient of the resistance at low temperatures.
منابع مشابه
Negative magnetoresistance in boron-doped nanocrystalline diamond films
Related Articles Room temperature deposition of alumina-doped zinc oxide on flexible substrates by direct pulsed laser recrystallization Appl. Phys. Lett. 100, 151902 (2012) Optimization of sputter deposition parameters for magnetostrictive Fe62Co19Ga19/Si(100) films J. Appl. Phys. 111, 07A939 (2012) Sign change in the organic magnetoresistance of tris(8-hydroxyquinolinato)aluminum upon anneali...
متن کاملEffect of Sn Doping on Structural and Optical Properties of 2D α-MoO3 Nanostructures
Undoped and Tin (Sn) doped Molybdenum trioxide (α-MoO3) nanostructured thin films (which has lamellar (2D) structure) have been prepared using a simple and cost effective technique of spray pyrolysis on glass substrates at 450 ℃. Surface morphology, optical and structural properties of samples have been investigated using FESEM, UV-Vis spectroscopy and XRD analysis techniques, respectively. FES...
متن کاملLattice and superexchange effects in doped CMRmanganites
We report on the influence of the lattice degrees of freedom on charge, orbital and spin correlations in colossal magnetoresistance (CMR) manganites. For the weakly doped compounds we demonstrate that the electron-phonon coupling promotes the trapping of charge carriers, the disappearance of the orbital polaron pattern and the breakdown of ferromagnetism at the CMR transition. The role of diffe...
متن کاملMicrostructure and inter-grain magnetoresistance in Ag-doped polycrystalline La0.67Sr0.33MnO3 thin films
Ag-doped La0.67Sr0.33MnO3 thin films with various Ag concentrations were deposited on (001) LaAlO3 substrates at 400 ◦C by using a dual-beam pulsedlaser deposition system. The Ag-doped films show polycrystalline structure with epitaxial c-axis columns. These columns were composed of closely arranged polyhedra of size 10–15 nm, resulting from the enhanced stressinduced grain boundary diffusion. ...
متن کامل