Effects of Nano-SiO2 on Setting Time and Compressive Strength of Alkali- activated Metakaolin-based Geopolymer
نویسندگان
چکیده
This study presents a discussion on the effects of different solid-to-liquid (S/L) ratios (0.97 to 1.19) and nanoSiO2 (NS) percentages (0% to 3%) on some properties of metakaolin (MK)-based geopolymers. The setting time and compressive strength were investigated. Mercury intrusion porosimetry, fourier transform infrared spectroscopy, and scanning electron microscopy were used to determine the microstructure of the samples. The results show that a MKbased geopolymer sample added 1% NS with the S/L ratio of 1.03 exhibits more strength and less porosity. Applying NS to the geopolymer enhances compactness and increases strength. Therefore, nanotechnology can be used to improve geopolymers.
منابع مشابه
Optimizing the Properties of Metakaolin-based (Na, K)-Geopolymer Using Taguchi Design Method
Geopolymer paste is an innovative construction material which shall be produced by chemical action of inorganic molecules. It is a more environmentally friendly alternative to conventional Portland cement which is abundantly available worldwide. In this study, the influence of different alkaline activators (Na and K) on the mechanical and thermal behaviors of metakaolin-based geopolymer was inv...
متن کاملPreparation and Properties of Alkali Activated Metakaolin-Based Geopolymer
The effective activation and utilization of metakaolin as an alkali activated geopolymer precursor and its use in concrete surface protection is of great interest. In this paper, the formula of alkali activated metakaolin-based geopolymers was studied using an orthogonal experimental design. It was found that the optimal geopolymer was prepared with metakaolin, sodium hydroxide, sodium silicate...
متن کاملEFFECT OF CALCINATION TEMPERATURE OF THE KAOLIN AND MOLAR Na2O/SiO2 ACTIVATOR RATIO ON PHYSICAL AND MICROSTRUCTURAL PROPERTIES OF METAKAOLIN BASED GEOPOLYMERS
Metakaolinite-based geopolymer has been synthesized at about 25 °C from metakaolin which has been calcined in different temperatures (600-900 °C) and different Na2O/SiO2 ratio activator (0.3-1.1). Compressive strength and microstructure of cement pastes after 7-28 days curing at ambient temperature were measured. Compressive strength tests on the samples showed that the sample made with calcine...
متن کاملModeling of Compressive Strength of Metakaolin Based Geopolymers by The Use of Artificial Neural Network RESEARCH NOTE)
In order to study the effect of R2O/Al2O3 (where R=Na or K), SiO2/Al2O3, Na2O/K2O and H2O/R2O molar ratios on the compressive strength (CS) of Metakaolin base geopolymers, more than forty data were gathered from literature. To increase the number of data, some experiments were also designed. The resulted data were utilized to train and test the three layer artificial neural network (ANN). Bayes...
متن کاملTaftan Pozzolan-Based Geopolymer Cement
Abstract: In recent years, many research works have been done to investigate the possibility of utilizing a broad range of materials as raw materials in the production of geopolymer cements. The use of artificial pozzolans or aluminosilicate-type industrial waste materials such as granulated blast-furnace slag and fly ash has been reported in many research works. Natural pozzolans are also al...
متن کامل