Effect of Water Nutrient Pollution on Long-Term Corrosion of 90:10 Copper Nickel Alloy

نویسنده

  • Robert E. Melchers
چکیده

Due to their good corrosion resistance, copper and copper alloys such as 90:10 Cu-Ni are used extensively in high-quality marine and industrial piping systems and also in marine, urban, and industrial environments. Their corrosion loss and pitting behaviour tends to follow a bi-modal trend rather than the classic power law. Field data for 90:10 copper nickel immersed in natural seawater are used to explore the effect of water pollution and in particular the availability of critical nutrients for microbiologically induced corrosion. It is shown, qualitatively, that increased dissolved inorganic nitrogen increases corrosion predominantly in the second, long-term, mode of the model. Other, less pronounced, influences are salinity and dissolved oxygen concentration.

برای دانلود رایگان متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Long-Term Corrosion Protection of a Cupro-Nickel Alloy Due to Graphene Coating

This study demonstrates the corrosion resistance of a Cu-Ni alloy coated with a multi-layer graphene. This is one of the first demonstrations of long-term corrosion resistance due to graphene coating, which is crucial since earlier studies have suggested graphene-coated copper to be considerably inferior to bare copper in terms of corrosion during long-term exposure to a corrosive environment. ...

متن کامل

Accelerated Degradation Test and Predictive Failure Analysis of B10 Copper-Nickel Alloy under Marine Environmental Conditions

This paper studies the corrosion behavior of B10 copper-nickel alloy in marine environment. Accelerated degradation test under marine environmental conditions was designed and performed based on the accelerated testing principle and the corrosion degradation mechanism. With the prolongation of marine corrosion time, the thickness of Cu₂O film increased gradually. Its corrosion product was Cu₂(O...

متن کامل

مقایسه فوق آب‌گریزی و رفتار خوردگی پوشش‌های میکرو- نانو ساختار نیکل و نیکل- کبالت بر روی زیرلایه مس

Super-hydrophobic nickel and nickel-cobalt alloy coatings with micro-nano structure were successfully electrodeposited on copper substrates with one and two steps electrodeposition. Surface morphology, wettability and corrosion  resistance were characterized by scanning electron microscopy, water contact angle measurements, electrochemical impedanc spectroscopy (EIS) and potentiodynamic...

متن کامل

EFFECT OF ANODIC OXIDATION ON THE CORROSION BEHAVIOR OF NICKEL-TITANIUM SHAPE MEMORY ALLOYS IN SIMULATED BODY FLUIDS (SBF)

The effect of anodic oxidation of a NiTi shape memory alloy in sulfuric acid electrolyte on its surface characteristics was studied. Surface roughness was measured by roughness tester. Surface morphology was studied using optical microscopy (OM) and scanning electron microscopy (SEM). Corrosion behavior was specified by recording Potentiodynamic polarization cur...

متن کامل

IJESRT INTERNATIONAL JOURNAL OF ENGINEERING SCIENCES & RESEARCH TECHNOLOGY Zn - Ni Alloy Deposit for Cadmium Replacement Applications

Zinc nickel alloy was deposited from alkaline bath at a PH of 13-14 with the nickel percentage of 5-9% in our prior research. Present study dealt with the research on 10-12% of Nickel at a PH of 12-13 from Zinc – nickel alloy electrolyte and the remaining percentage of Zinc, required for corrosion resistant applications to be used for reliable alternative of cadmium. Hull cell studies was carri...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

عنوان ژورنال:

دوره 8  شماره 

صفحات  -

تاریخ انتشار 2015