investigation on magnetic and microwave behavior of magnetite nanoparticles coated carbon fibers composite

نویسندگان

karim osouli

abbas kianvash

aliakbar entezami

چکیده

radar absorbing materials, i.e. magnetite (fe3o4) coated carbon fibers (mccfs) were fabricated by electro-deposition technique. black-colored single spinel phase fe3o4 nanoparticles was easily synthesized by hydrothermal method using reduction of a fe (iii) - triethanolamine complex in an aqueous alkaline solution at 60-80 ◦c. uniform and compact fe3o4 films were fabricated on nitric acid treated carbon fibers. a correlation between magnetic and absorption properties of specimens was made. it was found that the deposition time, and the sequences of the coating process have a significant effect on the reflection loss characteristics of the mccfs. on the other hand, the temperature of the coating process affects strongly the composition of the thin film. mccfs prepared at 80 ◦c possesses a much higher loss factor than the one prepared at 60 ◦c. the morphology, phases in the coating layer, magnetic properties and absorption behaviors of the mccfs were examined using fesem, xrd, permagraph, vector network analyzer (vna), respectively. the highest reflection loss that is −10 db at 12.27 ghz was observed in the sample deposited for four minutes. it was also found out that a uniform deposition layer can be observed in the sample deposited in three steps in which each step takes four minimums.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Investigation on magnetic and microwave behavior of magnetite nanoparticles coated carbon fibers composite

Radar absorbing materials, i.e. magnetite (Fe3O4) coated carbon fibers (MCCFs) were fabricated by electro-deposition technique. Black-colored single spinel phase Fe3O4 nanoparticles was easily synthesized by hydrothermal method using reduction of a Fe (III) - Triethanolamine complex in an aqueous alkaline solution at 60-80 ◦C. Uniform and compact Fe3O4 films were fabricated on nitric acid treat...

متن کامل

Microwave Synthesis and Magnetic Investigation of CuFe2O4 Nanoparticles and Poly Styrene-Carbon Nanotubes Composites

At the first step CuFe2O4 nanoparticles were synthesized by a fast and facile microwave method. The obtained nanoparticles and modified carbon nano tubes were added to poly styrene matrix. The products were characterized through Fourier transform infrared spectroscopy, X-ray diffraction, and scanning electron microscopy. Vibrating sample magnetometer shows nanoparticles exhibit ferromagnetic be...

متن کامل

microwave synthesis and magnetic investigation of cufe2o4 nanoparticles and poly styrene-carbon nanotubes composites

at the first step cufe2o4 nanoparticles were synthesized by a fast and facile microwave method. the obtained nanoparticles and modified carbon nano tubes were added to poly styrene matrix. the products were characterized through fourier transform infrared spectroscopy, x-ray diffraction, and scanning electron microscopy. vibrating sample magnetometer shows nanoparticles exhibit ferromagnetic be...

متن کامل

An investigation on synthesis and magnetic properties of nanoparticles of Cobalt Ferrite coated with SiO2

SiO2-coated Cobalt Ferrite (CoFe2O4) nanoparticles were obtained by the hydrolysis of tetraethylorthosilicate in the presence of CoFe2O4 nanoparticles in co-precipitation. The effects of SiO2coating on the magnetic properties of CoFe2O4 nanoparticles were investigated. The structural, morphological and magne...

متن کامل

investigation of effective parameters on the rigidity of light composite diaphragms (psscb) by fem

در این رساله با معرفی سقف های psscb متشکل از ترکیب ورق های فولادی ذوزنقه ای و تخته های سیمانی الیافی به عنوان سقف های پیش ساخته (سازگار با سیستم سازه ای قاب های فولادی سبک) به بررسی پارامترهای موثر بر صلبیت سقف، پرداخته می شود. در تحقیق حاضر ابتدا به مدل سازی دو نمونه سقف آزمایش شده، به روش اجزاء محدود با استفاده از نرم افزار تحلیلی abaqus ver 6.10 پرداخته شده است. نمونه های ساخته شده تحت اعما...

An investigation on synthesis and magnetic properties of nanoparticles of Cobalt Ferrite coated with SiO2

SiO2-coated Cobalt Ferrite (CoFe2O4) nanoparticles were obtained by the hydrolysis of tetraethylorthosilicate in the presence of CoFe2O4 nanoparticles in co-precipitation. The effects of SiO2coating on the magnetic properties of CoFe2O4 nanoparticles were investigated. The structural, morphological and magne...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
journal of particle science & technology

ناشر: iranian research organization for science and technology

ISSN 2423-4087

دوره 1

شماره 2 2015

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023