the structure-property relationship in a desulfurised and degassing hot work w500 tool steel

نویسندگان

m. kalantar

s. s. ghasemi

m. h. saadati

چکیده

the effect of secondary steelmaking processes such as desulphurization, removal of inclusions and vacuumdegassing followed by hot forging and hardening heat treatment on the microstructure and mechanical properties of a hot-work w500 tool steel have been studied in details. in order to follow the progress of secondary steel making, the content of impurity elements such as s, p, o, h and n were measured. these elements influence the mechanical testing and the microstructure of the steel. the results show that desulfurization treatment can be accelerated at higher temperature of 1680 °c and 15 minutes holding time for silicon and aluminum with contents of 0.33% and 0.056% in the molten steel, respectively. in this condition, the removal percentage of sulfur has been reached to about 90% relative to the initial sulfur content. for the degassing sample a, the strength and the hardness, after hot working and quenching – tempering, have been increased from 976 to 2020 mpa and 29 to 52 rc, respectively. whereas for the normal sample b, the associated strength and the hardness have been changed from 870 to 1845 mpa and 21 to 55 rc, respectively. the difference between mechanical properties of sample a and sample b cab be related to the presence of al2o3 clusters, silicate inclusions, and a longer filamentary inclusion in the microstructure of sample b after hot-forging. microstructural observations show that the morphology of pearlite in the forged sample a is more uniform and carbide particles are also much finer than these particles in the non-degassing forged sample b.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

The structure-property relationship in a desulfurised and degassing hot work W500 tool steel

The effect of secondary steelmaking processes such as desulphurization, removal of inclusions and vacuum degassing followed by hot forging and hardening heat treatment on the microstructure and mechanical properties of a hot-work w500 tool steel have been studied in details. In order to follow the progress of secondary steel making, the content of impurity elements such as S, P, O, H and N were...

متن کامل

EVALUATION OF THE MECHANICAL PROPERTIES OF NIOBIUM MODIFIED CAST AISI H 13 HOT WORK TOOL STEEL

Abstract: mechanical properties of AISIH 13 hot-work tool steel have been studied. Cast samples made of the modified new steel were homogenized and austenitized at different conditions, followed by tempering at the specified temperature ranges. Hardness, red hardness, three point bending test and Charpy impact test were carried out to evaluate the mechanical properties together with characteriz...

متن کامل

Laser Grooving of Surface Cracks on Hot Work Tool Steel

Repair welding (RW) with wire cladding is a common procedure to extend the in-service life of heavily loaded tool parts for die and mould industries 1-5 . The main advantages of repair welding are short downtime and cost efficiency compared to production of new tool part. Repair welding in general lowers the tool cost in the final part and enables higher added value to the die casting and injec...

متن کامل

a comparative study of the relationship between self-, peer-, and teacher-assessments in productive skills

تمایل به ارزیابی جایگزین و تعویض آن با آزمون سنتی مداد و کاغذ در سالهای اخیر افزایش یافته است. اکثر زبان آموزان در کلاس های زبان از نمره نهایی که استاد تعیین میکند ناراضی اند. این تحقیق جهت بررسی ارزیابی در کلاس های زبان انگلیسی به هدف رضایتمندی زبان آموزان از نمره هایشان انجام گرفته است که در آن نمرات ارائه شده توسط سه گروه ارزیاب (ارزیابی خود دانشجو، همسالان واستاد) در مهارت های تولید (تکل...

15 صفحه اول

the relationship between language and social capital in ilami kurdish: a sociopragmatic approach

چکیده زبان به عنوان یک وسیله در ایجاد و بازسازی سرمایه اجتماعی در چند دهه گذشته مورد توجه بوده است. اگر چه درباره سرمایه اجتماعی و سازه های مربوط به آن زیاد نوشته شده است ولی خیلی کم بر روی اینکه چطور زبان می تواند باعث ایجاد اعتماد یا بی اعتمادی بشود مطالعه ای انجام شده است. این مطالعه به منظور تحقق دو هدف انجام گرفته است. اول تلاش خواهد شد تا یک گونه شناسی از واژگانی که مردم کرد زبان شهر ا...

15 صفحه اول

this study investigated the relationship between quality of work life and organization citizenship behavior from the viewpoint of teachers in high schools in tehran city.

چکیده هدف از پژوهش حاضر بررسی رابطه کیفیت زندگی کاری و رفتار شهروندی سازمانی در مدارس مقطع متوسطه پسرانه شهر تهران از دیدگاه دبیران بود. روش پژوهش حاضر توصیفی و از نوع همبستگی بود. از بین دبیران مدارس شهر تهران تعداد 380 نفر به روش نمونه گیری خوشه ای چند مرحله ای به عنوان نمونه پژوهش انتخاب شدند و با تکمیل پرسشنامه ی کیفیت زندگی کاری والتون(1975) و پرسشنامه ی رفتار شهروندی سازمانی پودساکو...

15 صفحه اول

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
international journal of iron & steel society of iran

ناشر: iron & steel society of iran

ISSN 1735-4145

دوره 8

شماره 1 2011

کلمات کلیدی

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023