the effect of mechanical activation on the carbothermic reduction kinetics of hematite-graphite mixture

نویسندگان

f. mohseni

m. h. abbasi

m. panjepour

چکیده

the effect of mechanical activation on structural changes and kinetics of carbothermic reduction of hematite with graphite was studied in this research. hematite powder mixture with graphite (with stoichiometry ratio c/o=1) was milled for the time periods of zero to 50 hours, and the structural changes were studied using x ray diffraction (xrd). the effect of mechanical activation on the kinetics of hematite carbothermic reduction was studied by performing thermal analysis tests and by employing model-free and constant slope methods. the activation energy as well as the reaction mechanism was then determined. the results showed that by mechanical activation for a time period of 50 h, the activation energy is decreased from 387 kj/mol-1 to 186 kj/mol-1, and the starting temperature of the reaction is decreased from 1125 to 620°c. the boudouard chemical reaction was determined as the rate controlling step.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

The effect of mechanical activation on the carbothermic reduction kinetics of hematite-graphite mixture

The effect of mechanical activation on structural changes and kinetics of carbothermic reduction of hematite with graphite was studied in this research. Hematite powder mixture with graphite (with stoichiometry ratio C/O=1) was milled for the time periods of zero to 50 hours, and the structural changes were studied using X ray diffraction (XRD). The effect of mechanical activation on the kineti...

متن کامل

the effect of consciousness raising (c-r) on the reduction of translational errors: a case study

در دوره های آموزش ترجمه استادان بیشتر سعی دارند دانشجویان را با انواع متون آشنا سازند، درحالی که کمتر به خطاهای مکرر آنان در متن ترجمه شده می پردازند. اهمیت تحقیق حاضر مبنی بر ارتکاب مکرر خطاهای ترجمانی حتی بعد از گذراندن دوره های تخصصی ترجمه از سوی دانشجویان است. هدف از آن تاکید بر خطاهای رایج میان دانشجویان مترجمی و کاهش این خطاها با افزایش آگاهی و هوشیاری دانشجویان از بروز آنها است.از آنجا ک...

15 صفحه اول

the effect of mechanical activation and sodium carbonate on the kinetics of molybdenite carbothermic reduction

in this research, kinetics of carbothermic reduction of molybdenite in the presence of different amounts of sodium carbonate has been studied. mixed powders consisting of molybdenite, graphite and sodium carbonate with three mole-ratios of 1:4:2,1:4:3 and 1:4:4 were mechanically activated for 40 hours. the results of x-ray diffraction on activated samples showed that no reaction occurrs in diff...

متن کامل

the effect of taftan pozzolan on the compressive strength of concrete in the environmental conditions of oman sea (chabahar port)

cement is an essential ingredient in the concrete buildings. for production of cement considerable amount of fossil fuel and electrical energy is consumed. on the other hand for generating one tone of portland cement, nearly one ton of carbon dioxide is released. it shows that 7 percent of the total released carbon dioxide in the world relates to the cement industry. considering ecological issu...

the washback effect of discretepoint vs. integrative tests on the retention of content in knowledge tests

در این پایان نامه تاثیر دو نوع تست جزیی نگر و کلی نگر بر به یادسپاری محتوا ارزیابی شده که نتایج نشان دهندهکارایی تستهای کلی نگر بیشتر از سایر آزمونها است

15 صفحه اول

the effect of traffic density on the accident externality from driving the case study of tehran

در این پژوهش به بررسی اثر افزایش ترافیک بر روی تعداد تصادفات پرداخته شده است. به این منظور 30 تقاطع در شهر تهران بطور تصادفی انتخاب گردید و تعداد تصادفات ماهیانه در این تقاطعات در طول سالهای 89-90 از سازمان کنترل ترافیک شهر تهران استخراج گردید و با استفاده از مدل داده های تابلویی و نرم افزار eviews مدل خطی و درجه دوم تخمین زده شد و در نهایت این نتیجه حاصل شد که تقاطعات پر ترافیک تر تعداد تصادفا...

15 صفحه اول

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
international journal of iron & steel society of iran

ناشر: iron & steel society of iran

ISSN 1735-4145

دوره 7

شماره 2 2010

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023