improving the microstructure, mechanical and magnetic properties of aisi 4340 steel using the heat treatment process

نویسندگان

z. samadi shahreza

g. dini

a. taherizadeh

چکیده

aisi 4340 steel is one of the super strong steels that can be selected for different applications. by designing theproper cycles of heat treatment, the optimum microstructure and properties of this steel can be achieved. in thisstudy, different heat treatment cycles were introduced to achieve the optimum microstructure and improve themechanical and magnetic properties of aisi 4340 steel. the results of tensile, impact, hardness, metallographyand magnetic tests for various samples under different heat treatment cycles showed that parameters such astemperature and time of austenitizing and tempering were among the most important factors in achieving relativelya wide range of ultimate tensile strength (1467-933 mpa), impact energy (113-18 j), transport current density(1554-1347 mt), coercivity (1342-1240 a/m), diminished force (1165.6-947.5 mj/kg) and microstructure(tempered martensite and bainite). this wide range of properties can lead to a large number of applications of thistype of steel in various industries including manufacturing steel parts such as rotors.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Improving the Microstructure, Mechanical and Magnetic Properties of AISI 4340 Steel Using the Heat Treatment Process

AISI 4340 steel is one of the super strong steels that can be selected for different applications. By designing the proper cycles of heat treatment, the optimum microstructure and properties of this steel can be achieved. In this study, different heat treatment cycles were introduced to achieve the optimum microstructure and improve the mechanical and magnetic properties of AISI 4340 steel. The...

متن کامل

modification of nanoclay for improving the physico-mechanical properties of dental adhesives

هدف اصلی این مطالعه تهیه یک سامانه نوین چسب عاجی دندانی بر پایه نانورس پیوند شده با پلی متاکریلیک اسید، نانورس پیوند شده با پلی اکریلیک اسید، مخلوط نانوسیلیکا و نانورس پیوند شده با پلی متاکریلیک اسید، مخلوط نانوسیلیکا و نانورس پیوند شده با پلی اکریلیک اسید و نانورس پیوند شده با کیتوسان اصلاح شده با گلایسیدیل متاکریلات است. پیوند پلی متاکریلیک اسید و پلی اکریلیک اسید بر ری سطح نانورس در حضور و ...

Effect of Heat Treatment on Microstructure, Magnetic and Mechanical Properties of HSLA-100

In this study, the effects of various heat treatments on microstructure, mechanical and magnetic properties of HSLA-100 steel were evaluated. The heat treatments consisted of austenitizing at 900°C for 60 minutes, then quenching by different cooling rates via furnace, air, oil and water; and quenched specimens were aged at 600°C for one hour. Optical and field emission scanning electron m...

متن کامل

Investigation on Effect of Heat Input on the Microstructure and Mechanical Properties of Hadfield Steel Weld Joints in SMAW Process

In this investigation, the effect of heat input of SMAW process on the microstructure and mechanical properties of Hadfield steel weld joints was investigated. For this purpose, 4 annealed sheets with thickness 2 mm prepared from Hadfield steel and then welding applied by SMAW process with 6.75 and 11.25 kJ/mm heat input values. The evaluation of the microstructures of welding joints was condu...

متن کامل

Investigation on Effect of Heat Input on the Microstructure and Mechanical Properties of Hadfield Steel Weld Joints in SMAW Process

In this investigation, the effect of heat input of SMAW process on the microstructure and mechanical properties of Hadfield steel weld joints was investigated. For this purpose, 4 annealed sheets with thickness 2 mm prepared from Hadfield steel and then welding applied by SMAW process with 6.75 and 11.25 kJ/mm heat input values. The evaluation of the microstructures of welding joints was condu...

متن کامل

The Effect of Heat Treatment on Microstructure and Magnetic Properties of Nd17Fe76.5B5Cu1.5 Type Sintered Magnets

The effects of high temperature homogenization and low temperature annealing treatments on the microstructure and magnetic properties of sintered magnets of an Nd17Fe76.5B5Cu1.5 type alloy have been investigated. The microstructure of the as-cast alloy, consisted of three phases including a Nd2Fe14B1 (2:14:1- type) matrix phase Cu-containing Nd-rich Phase and Free α-iron. The as-sintered magnet...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
international journal of iron & steel society of iran

ناشر: iron & steel society of iran

ISSN 1735-4145

دوره 10

شماره 2 2013

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023