low temperature synthesis of α-fe2o3 nano-rods using simple chemical route

نویسندگان

m. farahmandjou

f. soflaee

چکیده

iron oxide (fe2o3) is widely used as a catalyst, pigment and gas sensitive material.  in this article, α-fe2o3 nano-rods were first synthesized via a simple chemical method using iron(iii) nitrate 9- hydrate (fe(no3)3.9h2o) as precursor. xrd pattern showed that the iron oxide nanoparticles exhibited alpha-fe2o3 (hematite) structure in nanocrystals. the single-phase α- fe2o3 nano-rods were prepared when the samples calcined at 500 °c. the smallest particle size was found to be 18 nm in diameter. the sem studies depicted rod-like shaped particles with formation of clusters by increasing annealing temperature. the sharp peaks in ftir spectrum determined the purity of fe2o3 nanoparticles and absorbance peak of uv-vis spectrum showed the small bandgap energy of 2.77 ev. the vsm result showed a coercive field and saturation magnetism around 90 g and 9.95 emu/g, respectively.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Low Temperature Synthesis of α-Fe2O3 Nano-rods Using Simple Chemical Route

Iron oxide (Fe2O3) is widely used as a catalyst, pigment and gas sensitive material.  In this article, α-Fe2O3 nano-rods were first synthesized via a simple chemical method using iron(III) nitrate 9- hydrate (Fe(NO3)3.9H2O) as precursor. XRD pattern showed that the iron oxide nanoparticles exhibited alpha-Fe2O3 (hematite) structure in nanocrystals. The single-phase α- Fe2O3 nano-rods were prepa...

متن کامل

synthesis of amido alkylnaphthols using nano-magnetic particles and surfactants

we used dbsa and nano-magnetic for the synthesis of amido alkylnaphtols.

15 صفحه اول

Characterization of γ- and α-Fe2O3 nano powders synthesized by emulsion precipitation-calcination route and rheological behaviour of α-Fe2O3

Nano crystals of γ-Fe2O3 (maghemite) were synthesized by emulsion precipitation method using kerosene as oil phase, SPAN80 (sorbitane monooleate) as the surfactant and sodium hydroxide as the precipitating agent. The characterization of the samples by FTIR (Fourier transform infra-red) and XRD (X-ray diffraction) techniques confirmed the formation of γ-Fe2O3 (maghemite). Analysis by SEM (scanni...

متن کامل

LOW TEMPERATURE MOLTEN SALT SYNTHESIS OF NANO CRYSTALLINE MgAl2O4 POWDER

Abstract: composition of MgO and nano boehmite. The reactant and potassium chloride, as the reaction media, were fired at800-1000 °C at different dwell times (0.5-5 h) in the ambient atmosphere. After washing and filtration, the spinel nanopowder was characterized by X-ray diffraction (XRD), Scanning electron microscopy (SEM), and Brunauer-Emmett-Teller (BET) techniques. It was demonstrated tha...

متن کامل

Synthesis and Characterization of α-Fe2O3 Nanoparticles by Simple Co-Precipitation Method

In the past decade, magnetic nanomaterials have attracted much attention due to their physical properties and technological applications. In this work, α-Fe2O3 nanoparticles were first synthesized via a simple co-precipitation method using iron chloride hexahydrate (FeCl3.6H2O) as precursor and ammonia solution as precipitator. The samples we...

متن کامل

Low-temperature synthesis route for YBa2Cu3Ox powder

• A submitted manuscript is the author's version of the article upon submission and before peer-review. There can be important differences between the submitted version and the official published version of record. People interested in the research are advised to contact the author for the final version of the publication, or visit the DOI to the publisher's website. • The final author version ...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
journal of nanostructures

ناشر: university of kashan

ISSN 2251-7871

دوره 4

شماره 4 2014

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023