the effect of length variation on the magnetic properties of nife alloy nanowires electrodeposited into the alumina template was investigated. the diameter (45±2.5 nm) and length (~ 1.9, 7.12, 8.3, 9.5 and 13.3 µm) of the nanowires were estimated from scanning electron microscopy images. energy dispersive spectroscopy results showed ni3fe7 composition of the alloy nanowires. the magnetic properties of the samples were investigated by vibrating sample magnetometer. it showed that with increasing the length of the nanowires from 1.9±0.1µm to 13.3±0.66 µm, coercivity reduced from 1050 oe to 705 oe and squareness reduced from 0.64 to 0.46. the results proved increasing the magnetostatic interaction between the nanowires with length. progress toward the multi-domain behavior was predicted caused to drastically reduce in the coercivity.
منابع مشابه
Magnetic Properties of Ni0.3Fe0.7 Alloy Nanowires
The effect of length variation on the magnetic properties of NiFe alloy nanowires electrodeposited into the alumina template was investigated. The diameter (45±2.5 nm) and length (~ 1.9, 7.12, 8.3, 9.5 and 13.3 µm) of the nanowires were estimated from scanning electron microscopy images. Energy dispersive spectroscopy results showed Ni3Fe7 composition of the alloy nanowire...
متن کاملMagnetic properties of single-crystalline CoSi nanowires.
We have observed unusual ferromagnetic properties in single-crystalline CoSi nanowire ensemble, in marked contrast to the diamagnetic CoSi in bulk. High-density freestanding CoSi nanowires with B20 crystal structure are synthesized by a vapor-transport-based method. The reaction of cobalt chloride precursor with a Si substrate produces high-aspect-ratio CoSi nanowires. The high-resolution trans...
متن کاملTuning the properties of magnetic nanowires
Magnetic nanorods or nanowires exhibit degrees of freedom associated with their inherent shape anisotropy and the ability to incorporate different components along their length. The introduction of multiple segments along the length of a nanowire can lead to further degrees of freedom associated with the shape of each segment and the coupling between layers. In this paper, we present an overvie...
متن کاملNanoporous pt-co alloy nanowires: fabrication, characterization, and electrocatalytic properties.
Nanoporous Pt-Co alloy nanowires were synthesized by electrodeposition of Co-rich Pt(1)Co(99) alloy into anodic aluminum oxide (AAO) membranes, followed by a dealloying treatment in a mild acidic medium. These nanowires consist of porous skeletons with tiny pores of 1-5 nm and crystalline ligaments of 2-8 nm. Morphological and compositional evolutions of the porous Pt-Co nanowires upon dealloyi...
متن کاملThe effect of pulsed electrodeposition parameters on the microstructure and magnetic properties of the CoNi nanowires
CoNi nanowires were deposited by pulsed electrodeposition technique into porous alumina templates. The effect of off time between pulses (toff) and reductive/oxidative time (treduc/oxid) on the microstructure and magnetic properties of the CoNi nanowires were investigated. Maximum coercivity and squareness were obtained for samples fabricated at treduc/oxid= 0.5 ms and toff =400 ms. The coerciv...
متن کاملInvestigations of Magnetic Properties Through Electrodeposition Current and Controlled Cu Content in Pulse Electrodeposited CoFeCu Nanowires
CoFeCu nanowires were deposited by pulsed electrodeposition technique into the porous alumina templates by a two-step mild anodization technique, using the single-bath method. The electrodeposition was performed in a constant electrolyte while Cu constant was controlled by electrodeposition current. The electrodeposition current was 3.5, 4.25, 5 and 6 mA. The effect of electrodeposition current...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
journal of nanostructuresناشر: university of kashan
ISSN 2251-7871
دوره 3
شماره 1 2013
کلمات کلیدی
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023