mixed matrix membranes prepared from high impact polystyrene with dispersed tio2 nanoparticles for gas separation

نویسندگان

p. safaei

a. marjani

m. salimi

چکیده

the current study presents synthesis and characterization of high impact polystyrene - tio2 nanoparticles mixed matrix membranes for separation of carbon dioxide from nitrogen. the solution-casting method was used for preparation of membranes. the nano mixed matrix membranes were characterized using scanning electron microscopy to ensure the suitable dispersion of nano particles in high impact polystyrene matrix. the effect of tio2 nanoparticles loading on membrane performance was investigated. the separation performance of synthesized membranes was investigated in separation of co2 from co2/n2 mixture. effect of feed pressure and tio2 content on separation of co2 was studied. the results revealed that increase of feed pressure decreases flux of gases through the mixed matrix membrane. the results also confirmed that the best separation performance can be obtained at tio2 nanoparticles loading of 7 wt.%.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Mixed matrix membranes prepared from high impact polystyrene with dispersed TiO2 nanoparticles for gas separation

The current study presents synthesis and characterization of high impact polystyrene - TiO2 nanoparticles mixed matrix membranes for separation of carbon dioxide from nitrogen. The solution-casting method was used for preparation of membranes. The nano mixed matrix membranes were characterized using scanning electron microscopy to ensure the suitable dispersion of nano particles in high impact ...

متن کامل

Polyurethane Mixed Matrix Membranes for Gas Separation: A Systematic Study on Effect of SiO2/TiO2 Nanoparticles

In this study, the effect of SiO2 and TiO2 nanoparticles on the gas separation performance of the polyurethane (PU) membranes has investigated. Polyurethanes were synthesized by bulk two step polym...

متن کامل

Mixed matrix membranes (MMMs) comprising organic polymers with dispersed inorganic fillers for gas separation

Gas separation by selective transport through polymeric membranes is one of the fastest growing branches of membrane technology. However, the existing polymeric membrane materials are inadequate to fully exploit the application opportunities on industrial scale; the improvement in permeability is at the expense of selectivity, and vice versa. A new type of membrane material emerging with the po...

متن کامل

Separation of Carbon Dioxide from Natural Gas by Matrimid-Based Mixed Matrix Membranes

Spherical MgO nanoparticles and Flake-like clay minerals modified with polyaniline (PAni) are applied in Matrimid in order to fabricate mixed matrix membranes (MMMs) having improved gas separation performance. The CO2 permeability, CO2/CH4 selectivity and CO2-induced plasticization pressure of MMMs are assessed at 4-30 bar feed pressure. The chemical structure, morphology and thermal properties...

متن کامل

Gas Separation Properties of Mixed Matrix Membranes based on Polyimide and Graphite Oxide

In this work, three different graphene-based materials, namely graphite oxide (GrO), thermally reduced graphite oxide (T-RGrO) and ascorbic acid multi-phase reduced graphene oxide (AMP-RGO), were synthesized and used to produce mixed matrix membranes (MMM) based on Matrimid®5218 for as separation. From the samples produced, a complete set of characterization was performed including XRD, FTIR, T...

متن کامل

Enhanced CO2/N2 separation performance by using dopamine/polyethyleneimine-grafted TiO2 nanoparticles filled PEBA mixed-matrix membranes

Mixed matrix membranes (MMMs) were fabricated by incorporating synthesized titanium dioxide (TiO2) nanoparticles into polyether block amide (PEBA) matrix to fabricate TiO2/PBEA MMMs for CO2/N2 separation. The mesoporous channels of TiO2 increased the density of active sites with high accessibility and also facilitate the diffusion of CO2 in the gas separation process. Furthermore, amine groups ...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
journal of nanostructures

ناشر: university of kashan

ISSN 2251-7871

دوره 6

شماره 1 2016

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023