effect of mineral trioxide aggregate, calcium enriched mixture and mineral trioxide aggregate with disodium hydrogen phosphate on bmp-2 production
نویسندگان
چکیده
introduction: one of the hypotheses regarding the calcification induction by mineral trioxide aggregate (mta) is the involvement of transforming growth factor-beta (tgf- β ) super family. calcium-enriched mixture (cem) cement is one of the endodontic biomaterials with clinical applications similar to mta. the aim of the present in vitro study was to compare the induction of bone morphogenic protein-2 (bmp-2) by a combination of disodium hydrogen phosphate (dshp) and tooth colored proroot mta (wmta), to that of cem cement and wmta. methods and materials: human gingival fibroblasts (hgfs) were obtained from the attached gingiva of human premolars. hgfs were cultured in dulbecco’s modified eagle’s medium, supplemented with 10% fetal calf serum, penicillin, and streptomycin. cells in groups 1, 2 and 3 were exposed to wmta, cem and wmta+dshp discs, respectively. the fourth group served as the control. after 72 h of exposure, hgf viability was determined by mosmann’s tetrazolium toxicity (mtt) assay. bmp-2 levels in cell-free culture media were determined by enzyme-linked immunosorbent assay (elisa). statistical analysis was performed using the one-way anova, followed by the post hoc games-howell test for bmp-2 and post hoc tukey’s test for the results of mtt assay. results: cellular viability was significantly higher in group 3 compared to the other groups ( p <0.05); however, cem and wmta did not exhibit significant differences ( p =0.08). the control group exhibited significantly higher cellular viability in comparison to the other groups of the study ( p <0.05). the highest and lowest protein production rates were observed in the wmta (3167±274.46 pg/ml) and wmta+dshp (1796±839.49 pg/ml) groups, respectively. there were no significant differences between the control, wmta and cem groups ( p >0.05). conclusion: wmta and cem did not exhibit any significant differences in inducing bmp-2 production compared to control; however, incorporation of dshp into wmta resulted in a decrease in the induction of this protein.
منابع مشابه
Effect of Mineral Trioxide Aggregate, Calcium-Enriched Mixture Cement and Mineral Trioxide Aggregate with Disodium Hydrogen Phosphate on BMP-2 Production
INTRODUCTION One of the hypotheses regarding the calcification induction by mineral trioxide aggregate (MTA) is the involvement of transforming growth factor-Beta (TGF-β) super family. Calcium-enriched mixture (CEM) cement is one of the endodontic biomaterials with clinical applications similar to MTA. The aim of the present in vitro study was to compare the induction of bone morphogenic protei...
متن کاملمقایسه واکنش زیرجلدی calcium enriched mixture (cem) و دو نوع mineral trioxide aggregate (mta) در rat
چکیده ندارد.
15 صفحه اولIn Vitro Cytotoxicity and Setting Time Assessment of Calcium-Enriched Mixture Cement, Retro Mineral Trioxide Aggregate and Mineral Trioxide Aggregate
Introduction The present study sought to evaluate and compare biocompatibility and setting time of Retro mineral trioxide aggregate (MTA), calcium-enriched mixture (CEM) and Angelus MTA. Methods and Materials CEM cement, Angelus MTA and Retro MTA were assessed in set and fresh states. Extracts transformed to each cavity of three 24-well plates in which 1×104 cell were seeded into each well 24...
متن کاملhistological evaluation of the effect of three medicaments; trichloracetic acid, formocresol and mineral trioxide aggregate on pulpotomized teeth of dogs
چکیده ندارد.
15 صفحه اولCondensation Pressure Effect on Microleakage of Mineral Trioxide Aggregate
Objective: The aim of this study is to measure the effect of different condensation pressure on the microleakage of Mineral Trioxide Aggregate (MTA). Methods: This study was an invitro study. A total of 55 single rooted straight-canal human extracted sound teeth free of cracks or calcification were selected. Teeth were sectioned from CEJ region at 3 mm above the root apex. Remaining specimens ...
متن کاملCompressive Strength of Mineral Trioxide Aggregate and Calcium-enriched Mixture Cement Mixed with Propylene Glycol
Introduction The aim of the present study was to evaluate and compare the compressive strength (CS) of mineral trioxide aggregate (MTA) and calcium-enriched mixture (CEM) cement when mixed with propylene glycol (PG). Methods and Materials Twenty four custom-made split molds with 5 holes in each were prepared. Molds were allocated into eight groups (n=15 holes) as follows: Groups 1,5: CEM and ...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
iranian endodontic journalجلد ۹، شماره ۳، صفحات ۲۲۰-۴
کلمات کلیدی
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023