synthesis and characterization of polyamide-66/calcium carbonate composites
نویسندگان
چکیده
polyamide-66(pa66)/caco3 micro- and nano-composites were prepared using a polymer solution method at filler loading of 0, 1, 2 and 3 weight percent. nano-size of caco3 was synthesized by micro-emulsion technique. the material was characterized by xrd, sem, ftir and uv-vis techniques. xrd results of composites suggested that caco3 particles are found in the amorphous phase of the semi-crystalline thermoplastic and α-crystalline form of thermoplastic is thermodynamically more stable than the γ-crystalline forms at room temperature. the uniform dispersion of 1, 2, and 3 wt. % surface modified micro- and nano-caco3within pa66 were evidenced from sem images. ft-ir analysis confirmed the chemical structure of the pa66. absorption peaks for all required chemical groups were showed in the ftir spectra: n-h stretch at 3305.52 cm-1, c-h stretch at 2865.02-2936.45 cm-1, amide-i at 1638.76 cm-1, and amide-ii at 1539.55 cm-1. uv-vis data showed that the presence of caco3 particles in pa66 results in the decrease of energy-band gaps of the composites. in addition, the results showed that incorporation of caco3 particles increased the modulus and tensile strength of neat pa66 however decreased its yield and elongation at break.
منابع مشابه
Synthesis and Characterization of Polyamide-66/Calcium Carbonate Composites
Polyamide-66(PA66)/CaCO3 micro- and nano-composites were prepared using a polymer solution method at filler loading of 0, 1, 2 and 3 weight percent. Nano-size of CaCO3 was synthesized by micro-emulsion technique. The material was characterized by XRD, SEM, FTIR and UV-VIS techniques. XRD results of composites suggested that CaCO3 particles are found in the amorphous phase of the semi-crystallin...
متن کاملsynthesis and characterization of some macrocyclic schiff bases
ماکروسیکلهای شیف باز از اهمیت زیادی در شیمی آلی و دارویی برخوردار می باشند. این ماکروسیکلها با دارابودن گروه های مناسب در مکانهای مناسب می توانند فلزاتی مثل مس، نیکل و ... را در حفره های خود به دام انداخته، کمپلکسهای پایدار تولید نمایند. در این پایان نامه ابتدا یک دی آلدئید آروماتیک از گلیسیرین تهیه می شود و در مرحله بعدی واکنش با دی آمینهای آروماتیک و یا آلیفاتیک در رقتهای بسیار زیاد منجر به ت...
15 صفحه اولSynthesis and Characterization of Polyamide Containing Maleimide Pendant Group
A series of new polyamides containing maleimide pendant group were prepared by low temperature polycondensation of 5-(4-(2,5-dioxo-2H-pyrrol-1(5H)-yl)benzamido)isophthaloyl chloride as a new monomer with various aromatic diamines in NMP. Monomer and polymers structures were identified through FT-IR, 1H-NMR and elemental analysis. Obtained polymers were soluble in polar solvents and non solu...
متن کاملsynthesis and characterization of potentially biological active cyclometallated organoplatinum(ii) complexes
this work is presented in five parts. in the first part preparation of the starting complex [pt(c^n)cl(dmso)], 1, in which c^n = n(1),c(2?)-chelated, deprotonated 2-phenylpyridine, and dmso = dimethylsulfoxide, and its reaction with 1 equiv of the biphosphine ligands bis(diphenylphosphino)amine, dppa, or bis(diphenylphosphino)methane, dppm, to give the complex [pt(c^n)cl(dppa)], 2, or [pt(c^n)c...
15 صفحه اولsynthesis and characterization of some new cyclometalated organoplatinum(ii) complexes containing phosphite ligand
در این تحقیق روشی جهت سنتز یک سری از کمپلکس های پلاتین (ii) حاوی لیگاند های دهنده ی فسفری شامل فسفیت و فسفین ارائه شده است. واکنش پیش ماده ی پلاتین (ii)،trans/cis- [ptcl2(sme2)2] ، با 2 اکی مولار از لیگاند p(oph)3در حلال بنزن کمپلکس1، cis-[ptcl2(p(oph)3)2] را تولید می نماید. جهت سنتز کمپلکس سایکلو متال فسفیتی، کمپلکس 1 با 1 اکی والان واکنشگر ptcl2 در حلال زایلن در شرایط رفلاکس زیر گاز آرگون م...
Synthesis of Polyaniline/Polyamide composites as membrane and investigation of its properties
Practical applications of conducting polymers such as polyaniline as membranes are particulary limitedbecause of their poor mechanical properties. However by mixing polyaniline with some conventional insulatingpolymers such as nylon and preparation composite films through solvent casting or blending, it seems to be asuitable way in order to increase the mechanical properties of the conducting p...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
journal of chemical and petroleum engineeringناشر: university of tehran
ISSN
دوره 49
شماره 1 2015
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023