fabrication parameters of asymmetric mixed matrix matrimid-mil-53/pmhs membrane for co2/ch4 separation
نویسندگان
چکیده
asymmetrically mixed matrix matrimid-mil-53 membranes with silicone cover layer were fabricated. for better understanding of membrane fabrication process, three main parameters of fabrication, matrimid concentration, silicone concentration and weight percentage of metal organic framework (mil-53) particles, were optimized by an experimental design method. cross-section sem images were used to study the membrane structure and polymer-particles interface. moreover, thermal resistance of the membranes and the existence of various bonds in them were investigated by ftir and tga analyses. the results showed that membranes had porous structure with finger-like morphology. at low and moderate percentages of particles, there were no non-selective voids observed at polymer-particles interface. the thermal resistance of membranes increased with the increase of mil-53 weight percentage and the destruction temperature of polymer increased from 410°c to 450°c. the permeability tests results showed that the matrimid (20% wt)-mil-53(15% wt)/pmhs (10%wt) membrane exhibited the highest level of co2/ch4 selectivity (23.6). however, in the membrane with 30 wt% particles loading, selectivity decreased due to particles agglomeration and void formation. the experimental design results showed that the concentration of silicone in covering solution had significant effect. co2 and ch4 permeability decreased and ideal selectivity of co2/ch4 increased with silicone concentration enhancement. although the matrimid concentration had a little effect on co2/ch4 ideal selectivity, its enhancement increased the selectivity of the gases. the optimization results showed the membrane with 17.8% of matrimd polymer, 13.2% of silicone polymer and 15.5 wt% of mil-53 particle displayed the highest selectivity and co2 permeability.
منابع مشابه
Separation of Carbon Dioxide from Natural Gas by Matrimid-Based Mixed Matrix Membranes
Spherical MgO nanoparticles and Flake-like clay minerals modified with polyaniline (PAni) are applied in Matrimid in order to fabricate mixed matrix membranes (MMMs) having improved gas separation performance. The CO2 permeability, CO2/CH4 selectivity and CO2-induced plasticization pressure of MMMs are assessed at 4-30 bar feed pressure. The chemical structure, morphology and thermal properties...
متن کاملFabrication and Characterization of Novel Mixed Matrix Polyethersulfone Based Nanofiltration Membrane Modified by Ilmenite (TECHNICAL NOTE)
This study is focused on fabrication and characterization of mixed matrix poly ether sulfone based nanofiltration membrane by phase inversion method. The effect of different amounts of Ilmenite (FeTiO3) particles as inorganic filler additive in the casting solution on physic-chemical characteristics of membranes was studied. Scanning electron microscopy, surface analysis, water content, contact...
متن کاملFabrication and Characterization of Novel Mixed Matrix Polyethersulfone Nanofiltration Membrane Modified by Iron-Nickel Oxide Nanoparticles
In this study, a mixed matrix polyethersulfone/iron-nickel oxide nanoparticle nanofiltration membrane was prepared by the solution casting technique. Polyvinylpyrrolidone was also used as a membrane pore former in membrane fabrication. The effect of iron-nickel oxide nanoparticles concentration in the casting solution on the membrane structure and performance was investigated. Scanning...
متن کاملDevelopment and Characterization of Defect-Free Matrimid® Mixed-Matrix Membranes Containing Activated Carbon Particles for Gas Separation
In this work, mixed-matrix membranes (MMMs) for gas separation in the form of thick films were prepared via the combination of the polymer Matrimid® 5218 and activated carbons (AC). The AC particles had a mean particle size of 1.5 μm and a mean pore diameter of 1.9 nm. The films were prepared by slow solvent evaporation from casting solutions in chloroform, which had a varying polymer–AC ratio....
متن کاملfabrication and characterization of novel mixed matrix polyethersulfone nanofiltration membrane modified by iron-nickel oxide nanoparticles
in this study, a mixed matrix polyethersulfone/iron-nickel oxide nanoparticle nanofiltration membrane was prepared by the solution casting technique. polyvinylpyrrolidone was also used as a membrane pore former in membrane fabrication. the effect of iron-nickel oxide nanoparticles concentration in the casting solution on the membrane structure and performance was investigated. scanning optical ...
متن کاملPolyurethane Mixed Matrix Membranes for Gas Separation: A Systematic Study on Effect of SiO2/TiO2 Nanoparticles
In this study, the effect of SiO2 and TiO2 nanoparticles on the gas separation performance of the polyurethane (PU) membranes has investigated. Polyurethanes were synthesized by bulk two step polym...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
علوم و تکنولوژی پلیمرجلد ۳۰، شماره ۱، صفحات ۶۳-۷۳
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023