fracture mechanics-based life prediction of a riveted lap joint

نویسندگان

a. r. shahani

h. moayeri kashani

چکیده

in this paper, three-dimensional modeling of the fatigue crack growth profiles was performed in a simple riveted lap joint. simulation results showed that mode i was dominated on the one side of the plates and the crack straightly grew on this side, while the other side of the plates was in a mixed-mode condition and the crack propagation path was not straight on this side. afterward, the fracture mechanics-based life prediction of the riveted lap joint was considered using eifs concept. back extrapolation method was used for estimating eifs. results demonstrated that eifs would depend on loading amplitude if δk had been implemented in eifs estimation using paris equation. in contrast eifs dependency on loading amplitude significantly reduced when using δj in eifs estimation. finally, fatigue life of the riveted lap joint was predicted based on safe life method using brown-miller critical plane criterion. results represented that the predicted life using fracture mechanics concept was much closer to the experimental results.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Fracture mechanics-based life prediction of a riveted lap joint

In this paper, three-dimensional modeling of the fatigue crack growth profiles was performed in a simple riveted lap joint. Simulation results showed that mode I was dominated on the one side of the plates and the crack straightly grew on this side, while the other side of the plates was in a mixed-mode condition and the crack propagation path was not straight on this side. Afterward, the fract...

متن کامل

On the Influence of Riveting Process Parameters on Fatigue Life of Riveted Lap Joint

In this paper, influence of riveting process parameters, namely, riveting force, sheet thickness, friction coefficient and clearance fit are investigated on residual stress field and fatigue life of single riveted lap joint of AA2024 type. According to the effect of riveting induced residual stresses on fatigue life of riveted lap joint, these parameters are optimized to maximize the residual s...

متن کامل

A Numerical Analysis of Riveted Lap Joint Containing Multiple-site Damage

The evaluation of stress intensity factors (SIFs) for cracks in mechanically fastened joints is one of the central issues in a damage tolerance analysis. Accurate stress intensity solutions may be difficult to determine due to geometric complexity along with variations in fastener load transfer and fastener interference and material thickness because of corrosion. Detailed finite element models...

متن کامل

A Comparison Study on Various Finite Element Models of Riveted Lap Joint by the Use of Dynamic Model Updating

Till now, various models have been proposed in literature to simulate the behavior of riveted structures. In order to find the most accurate analytical method in modeling the dynamic behavior of riveted structures, a comparison study is performed on several of these models, in this research. For this purpose, experimental modal analysis tests are conducted on a riveted plate to verify the effic...

متن کامل

Residual Strength Analyses of Riveted Lap-Splice Joints

Aging aircraft may develop multiple-site damage (MSD) that can reduce the structural integrity of fuselage structures. The existence of small cracks emanating from adjacent rivet holes in a fuselage lap-splice joint is of major concern. Small collinear cracks greatly reduce the residual strength of a panel with a lead crack. Recent studies predicting the residual strength of flat and curvilinea...

متن کامل

Probabilistic Fatigue Life Prediction of Bridge Cables Based on Multiscaling and Mesoscopic Fracture Mechanics

Abstract: Fatigue fracture of bridge stay-cables is usually a multiscale process as the crack grows from micro-scale to macro-scale. Such a process, however, is highly uncertain. In order to make a rational prediction of the residual life of bridge cables, a probabilistic fatigue approach is proposed, based on a comprehensive vehicle load model, finite element analysis and multiscaling and meso...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
journal of computational & applied research in mechanical engineering (jcarme)

ناشر: shahid rajaee teacher training university (srttu)

ISSN 2228-7922

دوره 4

شماره 1 2014

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023