study of effective parameters of coating on internal pores in cast iron parts produced by lost-foam casting

نویسندگان

عیسی امینی

جعفر خلیل علافی

رضا چاره خواه

زهرا معروفی

چکیده

in this study, the microstructure and properties of foam glass obtained as a result of the interaction of the waste glass with sic as the foaming agent and fe2o3 as the oxidizing agent have been investigated using scanning electron microscopy (sem), as well as three-point bending and pycnometery tests. first, the temperature and optimized amount of sic for making foam glass was determined. the results showed that the sample with 4% sic is changed into a foam at 850˚c with the highest percentage porosity (90%) and bending strength of 0.57 mpa, although the size of pores was relatively large and their distribution was heterogeneous. then, the effect of fe2o3 addition on the amount of porosity, microstructure and bending strength was taken into consideration, and the samples with smaller pores and homogenous pore distribution were obtained. moreover, the bending strength increased considerably in such a way that foam glasses with 61.4-73.2% porosity and 4.12-7.05 mpa bending strength were produced. these properties showed an enhancement when compared with those of the commercial samples.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

investigation of effective parameters on the rigidity of light composite diaphragms (psscb) by fem

در این رساله با معرفی سقف های psscb متشکل از ترکیب ورق های فولادی ذوزنقه ای و تخته های سیمانی الیافی به عنوان سقف های پیش ساخته (سازگار با سیستم سازه ای قاب های فولادی سبک) به بررسی پارامترهای موثر بر صلبیت سقف، پرداخته می شود. در تحقیق حاضر ابتدا به مدل سازی دو نمونه سقف آزمایش شده، به روش اجزاء محدود با استفاده از نرم افزار تحلیلی abaqus ver 6.10 پرداخته شده است. نمونه های ساخته شده تحت اعما...

Experimental Study of Effective Parameters on Honing Process of Cast Iron Cylinder

Honing is a process for finishing surfaces to obtain smooth surface. This process is used for final polish of inner parts such as engines cylinders. Optimizing this process has always been a big challenge for mass production of cylinder blocks of internal combustion engines. Honing process has some variable parameters, thus to get their optimum rates the automobile cylinders were tested. In thi...

متن کامل

Experimental Study of Effective Parameters on Honing Process of Cast Iron Cylinder

Honing is a process for finishing surfaces to obtain smooth surface. This process is used for final polish of inner parts such as engines cylinders. Optimizing this process has always been a big challenge for mass production of cylinder blocks of internal combustion engines. Honing process has some variable parameters, thus to get their optimum rates the automobile cylinders were tested. In thi...

متن کامل

study of cohesive devices in the textbook of english for the students of apsychology by rastegarpour

this study investigates the cohesive devices used in the textbook of english for the students of psychology. the research questions and hypotheses in the present study are based on what frequency and distribution of grammatical and lexical cohesive devices are. then, to answer the questions all grammatical and lexical cohesive devices in reading comprehension passages from 6 units of 21units th...

TiC Reinforcement Composite Coating Produced Using Graphite of the Cast Iron by Laser Cladding

In this study, a TiC-reinforced composite coating was produced to improve the wear resistance of a pearlite matrix grey iron using a pre-placed Ti powder by laser cladding. Results of scanning electron microscopy (SEM), X-ray diffractometer (XRD), and energy dispersive X-ray spectroscopy (EDS) confirmed that the coating was composed of TiC particles and two kinds of α-Fe phase. The fine TiC par...

متن کامل

Behavior of Generated Gas in Lost Foam Casting

In the Lost Foam Casting process, melting point temperature of metal, as well as volume and rate of the foam degradation have significant effect on the mold filling pattern. Therefore, gas generation capacity and gas gap length are two important parameters for modeling of mold filling time of the lost foam casting processes. In this paper, the gas gap length at the liquidfoam interface for a lo...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
مهندسی متالورژی و مواد

جلد ۲۴، شماره ۱، صفحات ۰-۰

کلمات کلیدی

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023