a research on surface oxidation of co67fe4cr7si8b14 amorphous ribbon during crystallization
نویسندگان
چکیده
deterioration of soft magnetic properties of amorphous ribbons happens when oxygen atoms diffuse in matrix during heat treatment. in this research, surface oxidation of co67fe4cr7si8b14 amorphous ribbons prepared by planar flow melt spinning (pfms) process during crystallization was investigated. in the first step, thermal stability of the ribbons was studied by differential thermal analysis (dta). amorphous samples were then annealed isothermally in argon atmosphere with 0.2% oxygen for 30 minutes at the temperature range of 350-650 ºc with 50 ºc interval. heat treated samples were studied by x-ray diffraction (xrd) analysis, scanning electron microscopy (sem) and energy dispersive spectroscopy (eds) analysis. according to the results, surface oxidation started around 550ºc. the oxide was found to be sio2 with amorphous structure. an increase in the temperature up to 600ºc, no crystalline phases was recognized by xrd in the sample annealed at this temperature, which can be attributed to increasing the thickness and continuity of the oxide layer. for the temperatures above 600ºc, the instability and discontinuity of the oxide layer were observed in some areas. in these areas, oxygen diffused in the matrix and combined with cobalt as coo, was also observed.
منابع مشابه
Oxidation and crystallization of an amorphous Zr60Al15Ni25 alloy
The amorphous ternary metallic alloy Zr60Al15Ni25 was oxidized in dry oxygen in the temperature range 310 ±C to 410 ±C. Rutherford backscattering (RBS) and cross-sectional transmission electron microscopy (TEM) studies suggest that during this treatment an amorphous layer of zirconium-aluminum-oxide is formed at the surface. Nickel was depleted in the oxide and enriched in the amorphous alloy n...
متن کاملCrystallization Kinetics Study in Al87Ni10La3 Amorphous Alloy
In this study, the crystallization behavior of melt-spun Al87Ni10La3 amorphous phase was investigated by using X-ray diffraction and non-isothermal differential thermal analysis techniques. The results demonstrated that the amorphous phase exhibited two-stage crystallization on heating, i.e., at first step the amorphous phase transforms into α-Al phase and at second step Al11La3 and Al3Ni inter...
متن کاملNon-isothermal Primary Crystallization Kinetics of the Amorphous Fe85.3B11P3Cu0.7 Alloy
In the present research, the primary crystallization kinetics of the amorphous Fe85.3B11P3Cu0.7 alloy was analyzed using non-isothermal DSC measurements. The average and local activation energies, Ea, were determined by different isokinetic and isoconversional methods. The results obtained for activation energy in this research, show that due to the complexity of the primary crystallization pro...
متن کاملSimultaneous crystalline-amorphous phase evolution during crystallization of polymer systems
– Despite the fact that polymer crystallization has been the object of intense research, this process is far from being fully understood. Traditional polymer crystallization studies using X-ray scattering techniques mainly provide information about the ordered regions. To obtain a more complete information about the time evolution of both the crystalline and the amorphous phase during polymer c...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
مهندسی متالورژی و موادجلد ۲۴، شماره ۲، صفحات ۰-۰
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023