effect of mechanical loads and surface roughness on wear of silorane and methacrylate-based posterior composites

نویسندگان

masumeh hasani tabatabaei tehran university of medical sciences

sakineh arami tehran university of medical sciences

farnaz farahat shahid sadoughi university of medical sciences

چکیده

objectives: dental composite wear in posterior restorations is a concern and is affected by different factors. this study was conducted to evaluate the effect of polishing and mechanical loads on wear of silorane-based and methyl methacrylate-based composites resins. materials and methods: of each dental composite (filtek p90 and filtek p60), 40 samples were fabricated in a polyethylene mold (4mm diameter, 10mm height). according to the finishing and/or polishing protocols (180-grit or 2500-grit silicon carbide papers), the samples of each composite were divided into two groups. surface roughness (rₔ) was measured and recorded using a contact profilometer. the weight of each sample was also measured in grams. the wear test was performed in a pin-on-disc device under two different loads (70n, 150n). afterwards, samples were subjected to profilometry and their weight was measured again. data were analyzed using t-test and univariate anova. p <0.05 was considered statistically significant. results: higher mechanical load resulted in greater weight loss (p<0.001). samples polished with 2500-grit papers showed significantly lower ra changes compared to those polished with 180-grit papers (p<0.001). filtek p90 had greater weight loss than filtek p60 except in one condition (180-grit, 70n). conclusions: results showed that wear of posterior composite restorations depends on mechanical load, type of composite resin and surface properties.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Effect of Mechanical Loads and Surface Roughness on Wear of Silorane and Methacrylate-Based Posterior Composites

OBJECTIVES Dental composite wear in posterior restorations is a concern and is affected by different factors. This study was conducted to evaluate the effect of polishing and mechanical loads on wear of silorane-based and methyl methacrylate-based composites resins. MATERIALS AND METHODS Of each dental composite (Filtek P90 and Filtek P60), 40 samples were fabricated in a polyethylene mold (4...

متن کامل

Effect of pre-heating on the mechanical properties of silorane-based and methacrylate-based composites

BACKGROUND The use of composites in dental restoration has been commonly criticized, due to their underwhelming mechanical properties. This problem may be solved partially by preheating. The present research aims to determine the effect of preheating on the mechanical properties of two different classes of composites. MATERIAL AND METHODS A Silorane-based (Silorane) and a Methacrylate-based (...

متن کامل

A Review of Silorane and Methacrylate Based Composites and Effective Factors on Microleakage of them

Introduction: An important disadvantage of current dental resin composites is their polymerization shrinkage and production of microleakage. This shrinkage can cause tooth sensitivity, marginal discoloration, and secondary caries. The objective of this study was to review the effective factors on microleakage of methacrylate and silorane composites and compare them with each other. This review...

متن کامل

effect of seed priming and irrigation regimes on yield,yield components and quality of safflowers cultivars

این مطالعه در سال 1386-87 در آزمایشگاه و مزرعه پژوهشی دانشگاه صنعتی اصفهان به منظور تعیین مناسب ترین تیمار بذری و ارزیابی اثر پرایمینگ بر روی سه رقم گلرنگ تحت سه رژیم آبیاری انجام گرفت. برخی از مطالعات اثرات سودمند پرایمینگ بذر را بر روی گیاهان مختلف بررسی کرده اند اما در حال حاضر اطلاعات کمی در مورد خصوصیات مربوط به جوانه زنی، مراحل نموی، عملکرد و خصوصیات کمی و کیفی بذور تیمار شده ژنوتیپ های م...

Effects of Carbamide Peroxide Bleaching Gel on Color of Silorane- and Methacrylate-based Resin Composites

Introdouction: Bleaching has become a common treatment for improving the appearance of natural teeth. However, the need to protect dental restorations from bleaching agent exposure is inevitable, as these agents may change the color of restorative materials by oxidation. Filtek P90 composite resin has recently been introduced with the aim of decreasing polymerization shrinkage. The purpose of...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
journal of dentistry, tehran university of medical sciences

جلد ۱۳، شماره ۶، صفحات ۴۰۷-۴۱۴

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023