effect of silane solvent on microtensile bond strength of hy-drogen peroxide-treated fiber post and composite core
نویسندگان
چکیده
objective: the aim of this in vitrostudy was to evaluate the effect of the type of solvent in silane solution on microtensile bond strength of fiber posts to composite resin cores af-ter application of 24% hydrogen peroxide. materials and methods: eighteen white fiber posts, immersed in 24% hydrogen peroxide were divided into three groups (n=6). in the group a post surfaces were silanized with an ethanol based solution, in group b with an acetone based solution, in the group c with and un-diluted methacryloxytrimethoxysilane (as the control group). the cores were built up using flowable composite. microtensile bond strength test and evaluations using stereomi-croscope were performed on the samples and the data were analyzed using one-way anova and tukey hsd tests. results: a significant difference was observed between the amounts of microtensile bond strength of fiber poststo composite cores in the groups a and b, and the ones in group c (p<0.05). there was no such difference between groups a and b (p>0.05). conclusion: the type of solvent in silane solution has no effect on microtensile bond strength between fiber post andcomposite resin core after application of 24% hydrogen peroxide.
منابع مشابه
Effect of silane activation on shear bond strength of fiber-reinforced composite post to resin cement
PURPOSE Among the surface treatment methods suggested to enhance the adhesion of resin cement to fiber-reinforced composite posts, conflicting results have been obtained with silanization. In this study, the effects of silanization, heat activation after silanization, on the bond strength between fiber-reinforced composite post and resin cement were determined. MATERIALS AND METHODS Six group...
متن کاملBond strength between fiber posts and composite resin core: influence of temperature on silane coupling agents.
This study evaluated the effect of air drying temperature and different silane coupling agents on the bond strength between glass fiber posts and composite resin core. The post surface was cleaned with alcohol and treated with different silane coupling agents, being three prehydrolyzed silanes [Silano (Angelus), Prosil (FGM), RelyX Ceramic Primer (3M ESPE)] and one two-component silane [Silane ...
متن کاملEffect of different synthetic matrix metalloproteinase inhibitors on composite-dentin microtensile bond strength durability
Background and Aims: Despite patient’s demand increased for tooth color restorations, the stable bond between dentin and composite is a challenge in dentistry. Dentin protease activation is responsible for dentin-resin bond failure. The aim of this study was to determine the best pretreatment agent to inhibit matrix metalloproteinase and increase resin-dentin bond durability. Materials and Met...
متن کاملEffect of Cementation Technique of Individually Formed Fiber-Reinforced Composite Post on Bond Strength and Microleakage
OBJECTIVES The aim of this study was to evaluate the effect of two different cementation techniques of individually formed E-glass fiber-reinforced composite (FRC) post on bond strength and microleakage. METHODS The crowns of extracted third molars were removed and post preparation was carried out with parapost drills (diameter 1.5 mm). After application of bonding agents individually formed ...
متن کاملEffect of CO2, Nd:YAG and Er:YAG Lasers on Microtensile Bond Strength of Composite to Bleached-Enamel
BACKGROUND Tooth restoration immediately after bleaching is challenging due to the potential problems in achieving adequate bond strength. OBJECTIVE The aim of this study was to evaluate the effect of surface treatment with ER:YAG, ND:YAG, CO2 lasers and 10% sodium ascorbate solution on immediate microtensile bond strength of composite resin to recently bleached enamel. MATERIALS & METHODS ...
متن کاملfracture strength of endodontically treated teeth restored with casting post and core and glass-fiber with composite core
introduction: prefabricated metal and ceramic posts can be used with different kinds of core materials as an alternative to the conventional casting post and cores. it is unclear how these post and core systems can withstand different kind of forces in the mouth. the purpose of this study was to compare the fracture strength of endodontically treated, crowned maxillary incisors restored with ca...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
journal of dentistry, tehran university of medical sciencesجلد ۵، شماره ۳، صفحات ۱۲۰-۱۲۵
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023