comparison of the amount of fluoride release from nanofilled resin modified glass ionomer, conventional and resin modified glass ionomer cements.

to investigate and compare the amount of fluoride release of conventional, resin modified and nanofilled resin modified glass ionomer cements.tablets of glass-ionomer cements were immersed in deionized water and incubated at 37°c. after 1, 2, 7, 15 and 30 days, fluoride ion was measured under normal atmospheric conditions by fluoride ion selective electrode. buffer (tisab ii) was used to decomplex the fluoride ion and to provide a constant background ionic strength and to maintain the ph of water between 5.0 and 5.5 as the fluoride electrode is sensitive to changes in ph. statistical evaluation was carried out by one way anova (analysis of variance) using spss 11.0. the significance level was set at p< 0.05.the release of fluoride was highest on day 1 and there was a sudden fall on day 2 in all three groups. initially fluoride release from conven-tional glass-ionomer cement was highest compared to the other two glass-ionomer cements, but the amount drastically reduced over the period. although the amount of fluoride release was less than both the resin modified and nanofilled resin modified glass-ionomer cement, the release was sustained consistently for 30 days.the cumulative fluoride release of nanofilled resin modified glass ionomer cement was very less compared to the conventional and resin modified glass ionomer cements and nanofilled resin modified glass ionomer cement released less but steady fluoride as compared to other resin modified glass ionomer cements.