effect of bioactive glass air abrasion on shear bond strength of two adhesive resins to decalcified enamel.

bioactive glass air abrasion is a conservative technique to remove initial decalcified tissue and caries. this study examined the shear bond strength of composite resin to sound and decalcified enamel air-abraded by bioactive glass (bag) or alumina using etch-and-rinse and self-etch adhesives.forty-eight permanent molars were root-amputated and sectioned mesiodistally. the obtained 96 specimens were mounted in acrylic resin; the buccal and lingual surfaces remained exposed. a demineralizing solution was used to decalcify half the specimens. both sound and decalcified specimens were divided into two groups of alumina and bioactive glass air abrasion. in each group, the specimens were subdivided into two subgroups of clearfil se bond or optibond fl adhesives (n=12). composite resin cylinders were bonded on enamel surfaces cured and underwent thermocycling. the specimens were tested for shear bond strength. data were analyzed using spss 16.0 and three-way anova (α=0.05). similar to the experimental groups, the enamel surface of one specimen underwent sem evaluation.no significant differences were observed in composite resin bond strength subsequent to alumina or bioactive glass air abrasion preparation techniques (p=0.987). there were no statistically significant differences between the bond strength of etch-and-rinse and self-etch adhesive groups (p=1). also, decalcified or intact enamel groups had no significant difference (p=0.918). however, sem analysis showed much less enamel irregularities with bag air abrasion compared to alumina air abrasion.under the limitations of this study, preparation of both intact and decalcified enamel surfaces with bioactive glass air abrasion results in similar bond strength of composite resin in comparison with alumina air abrasion using etch-&-rinse or self-etch adhesives.