effect of bonding application time on bond strength of composite resin to glass ionomer cement

نویسندگان

narges panahandeh

hassan torabzadeh

amir ghassemi

mina mahdian

چکیده

objectives : this experimental study evaluated the effect of bonding application time on the microshear bond strength of composite resin to different types of glass ionomer cements (gics). materials and methods: one-hundred and sixty specimens (two conventional and two resin-modified gics) were prepared and divided into 16 groups. the surface of all specimens was prepared using two different bonding systems (frog and stea) at three different times. after setting, the composite resin (z100) was placed over the gics. the specimens were then stored in distilled water for 24 hours (37oc) and exposed to microshear stresses at a crosshead speed of 1 mm/min. the results were analyzed using three-way anova and tukey’s test (p˂0.05). results: in conventional gics, bond strength was affected by the type of bonding system at different times, and bond strength was significantly higher in the fuji ii group compared to riva self cure group. in the riva self cure group, bond strength was significantly affected by time; whereas, the type of bonding system failed to exert a significant effect on bond strength. there was no significant correlation between the type of bonding system and the two brands of resin-modified gics. bond strength was not affected by the type of bonding agent; however, among the two brands of resin-modified gics, fuji ii lc yielded a significantly stronger bond. conclusion: it appears that the type of bonding agent does not affect the microshear bond strength, and the bonding application time affects the microshear bond strength in riva self cure gics.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Effect of Bonding Application Time on Bond Strength of Composite Resin to Glass Ionomer Cement

OBJECTIVES This experimental study evaluated the effect of bonding application time on the microshear bond strength of composite resin to different types of glass ionomer cements (GICs). MATERIALS AND METHODS One-hundred and sixty specimens (two conventional and two resin-modified GICs) were prepared and divided into 16 groups. The surface of all specimens was prepared using two different bon...

متن کامل

Shear bond strength evaluation of resin composite to resin-modified glass-ionomer cement using three different resin adhesives vs. glass-ionomer based adhesive

Background: The clinical success of sandwich technique depends on the strength of resin-modified glass ionomer cement (RMGIC) bonding to both dentin and resin composite. Therefore, the shear bond strength (SBS) of resin composite bonded to RMGIC utilizing different resin adhesives versus a GIC-based adhesive was compared. Materials and methods: In this in vitro study, 84 holes (5×2 mm) were pre...

متن کامل

Effect of etching and light-curing time on the shear bond strength of a resin-modified glass ionomer cement.

The aim of this study was to assess the influence of etching and light-curing time on the shear bond strength (SBS) and adhesive remnant index (ARI) of a resin-modified glass ionomer cement (RMGIC) upon debonding of orthodontic brackets. Sixty-eight bovine permanent incisors were obtained and embedded in acrylic resin. Edgewise metallic brackets were bonded to the teeth with Fuji Ortho LC RMGIC...

متن کامل

Fracture Strength of Severely Damaged Primary Anterior Teeth after Restoration with Composite Resin and Resin-Modified Glass Ionomer Cement

Background and Aim: Restoration of primary anterior teeth with severe caries extending to the gingival margin is challenging for many clinicians especially in uncooperative children. Resin modified glass ionomer cements (RMGICs) can be suitable for use in such cases since they require fewer application steps than composite resins. This study aimed to assess the fracture strength of severely dam...

متن کامل

Shear bond strength of resin modified glass ionomer cement bonded to different tooth-colored restorative materials.

AIM The aim of this study was to determine in vitro the shear bond strength (MPa) and the type of bond failure when resin-modified glass ionomer cement (RMGIC) was bonded with different tooth-colored restorative materials. METHODS AND MATERIALS The RMGIC tested was Fuji II LC (FL) and the tooth-colored restorative materials used were composite resin Point-4 (P4), Compomer Dyract AP (DY), and ...

متن کامل

Bond Strength of Resin-modified Glass Ionomer Adhesive to Dentin with Ethanol-wet Bonding

Background and Aim: The aim of the present study was to investigate adhesion ability of resin-modified glass ionomer adhesive (Vitrebond) to ethanol-saturated dentin following two different surface conditioning regimes in term of microtensile bond

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
journal of dentistry, tehran university of medical sciences

جلد ۱۲، شماره ۱۱، صفحات ۸۵۹-۸۶۷

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023