assessment of foolad mobarakeh st14 low carbon steel sheet for automobile frames
نویسندگان
چکیده
in this research formability behavior and texture of st14 low carbon steels produced by foolad mobarakeh plant for deep drawing application had been studied. plate textures were characterized by x-ray diffraction technique. to evaluate formability behavior one dimensional tensile test was carried out and related parameters were recognized. moreover eriksson experiment and spherical pattern printing on samples were also implemented to scheme ultimate formability curve (fld). ultimate formability curve area was calculated using plane strain variations (fld 0 ). effect of mechanical parameters on ultimate formability curve consist of yield strength, tensile strength, strain hardening coefficient, perpendicular anisotropy and texture were also studied. the results show that by increasing yield strength and tensile strength, lower area of ultimate formability curve decreases. in contrast by increasing total elongation, strain hardening coefficient and perpendicular anisotropy parameter, plate formability has been enhanced
منابع مشابه
Recrystallization Behavior of Deep Drawing Low Carbon Steel Sheets Produced by Mobarakeh Steel Plant
In the present work the recrystallization behavior of deep drawing grade Al-killed low carbon steel sheets produced by Mobarakeh Steel Plant (MSP) has been studied. Salt bath isothermal annealing has b...
متن کاملassessment of the park- ang damage index for performance levels of rc moment resisting frames
چکیده هدف اصلی از طراحی لرزه ای تامین ایمنی جانی در هنگام وقوع زلزله و تعمیر پذیر بودن سازه خسارت دیده، پس از وقوع زلزله است. تجربه زلزله های اخیر نشان داده است که ساختمان های طراحی شده با آیین نامه های مبتنی بر نیرو از نظر محدود نمودن خسارت وارده بر سازه دقت لازم را ندارند. این امر سبب پیدایش نسل جدید آیین نامه های مبتنی بر عملکرد شده است. در این آیین نامه ها بر اساس تغییرشکل های غیرارتجاعی ...
15 صفحه اولrecrystallization behavior of deep drawing low carbon steel sheets produced by mobarakeh steel plant
in the present work the recrystallization behavior of deep drawing grade al-killed low carbon steel sheets produced by mobarakeh steel plant (msp) has been studied. salt bath isothermal annealing has been applied to cold rolled samples and the resulted microstrucrures have been compared with the microstructure obtained from the box annealing process in msp. it is found that at 635 and 700ºc the...
متن کاملRobustness Assessment of Steel Moment Resisting Frames
Nowadays, many buildings with steel Moment Resisting Frames (MRF) are built in seismic zones when seismic codes are at its early stages of development, and as such, these structures are often designed solely to resist lateral wind loads without providing an overall ductile mechanism. On the other hand, current seismic design criteria based on hierarchy of resistance allow enhancing the structur...
متن کاملEffect of Ti-microalloy Addition on the Formability and Mechanical Properties of a Low Carbon (ST14) Steel
A low carbon Al-killed Ti-added steel was produced in Mobarakeh Steel Complex in Iran. Mechanical properties and microstructural characterizations of steel in the as-cast, hot-rolled, cold-rolled and annealed conditions are presented. Dilatometery tests were carried out to measure the finishing and annealing temperatures of steel. It was found that the addition of small amounts of Ti increas...
متن کاملLow-Carbon Steel Sheet Asymmetric Single-Point Incremental Forming: Analysis and Optimization of the Surface Roughness (TECHNICAL NOTE)
Surface roughness (SR) has an adverse effect on the appearance of low-carbon steel parts, formed in the asymmetric incremental sheet forming (AISF) process, particularly those requiring painting operation. The purpose of this study is to investigate the effects of AISF process parameters on the surface roughness of an asymmetric part formed on low-carbon steel sheets. The parameters are feed ra...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
international journal of advanced design and manufacturing technologyجلد ۱، شماره ۱، صفحات ۵۹-۶۶
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023