effect of resin cement pre-heating on the push-out bond strength of fiber post to root canal dentin

background and aims. various factors influence the interfacial bond between the fiber posts and root canal dentin. the aim of the present study was to evaluate the effect of pre-warming of resin cement on the push-out bond strength of fiber posts to various segments of root canal dentin. materials and methods. in this in vitro study, 40 single-rooted human premolars were decoronated and underwent root canal treatment along with post space preparation. the samples were randomly divided into two groups: in group 1, panavia f 2.0 cement was used at room temperature; in group 2, the same cement was warmed to 55‒60°c before mixing. after fiber posts were placed and cemented in the root canals, 3 dentin/post sections (coronal, middle and apical) with a thickness of 3 mm were prepared. a universal testing machine was used to measure push-out bond strength in mpa. data was analyzed using two-factor anova and a post hoc tukey test at α=0.05. results. the mean value of push-out bond strength was high at room temperature, and the differences in the means of push-out bond strength values between the resin cement temperatures and between different root segments in each temperature were significant (p<0.05). conclusion. pre-warming of panavia f 2.0 resin cement up to 55‒60°c reduced push-out bond strength to root canal dentin. in addition, in each temperature group bond strengths decreased from coronal to apical segments.