hot deformation behavior of 17-7 ph stainless steel

نویسندگان

mohammad zeinali

maleke ashtar university of technology ehsan shafiei

amirkabir university of technology k. farmanesh

maleke ashtar university of technology r. hosseini

shiraz university r. sooltanipor

چکیده

to investigate the hot deformation behavior of 17-7 ph stainless steel, hot compression tests were carried out at the temperatures of 950, 1050 and 1150 oc and strain rates of 0.001 s-1 to 0.1 s-1. accordingly, the hot working behavior was studied by the analyses of flow stress curves, work hardening rate versus stress curves, exponent- type constitutive equations and deformed microstructures. meanwhile, the average normalized critical stress for initiation of dynamic recrystallization (drx) was determined using a 3rd order polynomial curve fitting. the results show that the flow stress depends strongly on the deformation temperature and the strain rate, and it increases with the deformation temperature decreasing and the strain rate increasing. furthermore, it was found out that the co- existence of δ- ferrite lowers the softening rate at high z (zener- holloman parameter) conditions. the experimental results were then used to determine the constants of constitutive equations. there is a good agreement between the measured and predicted results indicating a high accuracy of exponent- type constitutive equations.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Hot Deformation Behavior of 17-7 PH Stainless Steel

To investigate the hot deformation behavior of 17-7 PH stainless steel, hot compression tests were carried out at the temperatures of 950, 1050 and 1150 oC and strain rates of 0.001 s-1 to 0.1 s-1. Accordingly, the hot working behavior was studied by the analyses of flow stress curves, work hardening rate versus stress curves, exponent- type constitutive equations and deformed microstructures. ...

متن کامل

Dynamic Recrystallization under Hot Deformation of a PH Stainless Steel

Dynamic recrystallization, DRX, behaviour of a precipitation hardened, PH, stainless steel was studied in connection with microstructural developments in a compression test. The experimental results showed that the dominant mechanism of softening is DRX, but at high strain rates and low temperatures, ie, high Zener-Holman parameter, Z, work hardening and dynamic recovery, DRV, produced a pancke...

متن کامل

dynamic recrystallization under hot deformation of a ph stainless steel

dynamic recrystallization, drx, behaviour of a precipitation hardened, ph, stainless steel was studied in connection with microstructural developments in a compression test. the experimental results showed that the dominant mechanism of softening is drx, but at high strain rates and low temperatures, ie, high zener-holman parameter, z, work hardening and dynamic recovery, drv, produced a pancke...

متن کامل

PREDICTION OF HOT DEFORMATION BEHAVIOUR OF A PH STAINLESS STEEL AT HIGH STRAIN RATES

In this study the hot deformation behaviour of a precipitation hardened (PH) stainless steel at high strain rates has been predicted through hot compression testing. Stress-strain curves were obtained for a range of strain rates from 10-3 to 10+1 S-1 and temperatures from 850 to 1150°C. Results obtained by microstructure and stress-strain curves show that at low temperatures and high strain rat...

متن کامل

Towards sustainable machining of 17-4 PH stainless steel using hybrid MQL-hot turning process

The use of a minimum quantity of lubrication (MQL) with extremely low consumption of lubricant in machining processes has been reported as a technologically and environmentally feasible alternative to conventional flood cooling. In hot machining, the external heat source is applied during machining that will assist to increase machining performance. Many external heating techniques are availabl...

متن کامل

EVALUATION OF PRECIPITATION HARDENING HEAT TREATMENT OF PH 17-7 STAINLESS STEEL SPRING

In this paper, the influence of heat treatment on PH17-7 stainless steel spring was evaluated. Precipitation hardening phenomenon of  PH 17-7 steel was evaluated in three stages. First, the spring constant changes with time and temperature was evaluated. Second, the spring constant changes with respect to its original length at constant temperature and time with blocking (spring length aft...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
iranian journal of materials forming

جلد ۴، شماره ۱، صفحات ۱-۱۱

کلمات کلیدی
[ ' h o t d e f o r m a t i o n ' , ' d y n a m i c r e c r y s t a l l i z a t i o n ' , ' c o n s t i t u t i v e a n a l y s i s ' , 1 7 , ' 7 p h s t a i n l e s s s t e e l ' ]