hot deformation behavior of 17-7 ph stainless steel
نویسندگان
چکیده
to investigate the hot deformation behavior of 17-7 ph stainless steel, hot compression tests were carried out at the temperatures of 950, 1050 and 1150 oc and strain rates of 0.001 s-1 to 0.1 s-1. accordingly, the hot working behavior was studied by the analyses of flow stress curves, work hardening rate versus stress curves, exponent- type constitutive equations and deformed microstructures. meanwhile, the average normalized critical stress for initiation of dynamic recrystallization (drx) was determined using a 3rd order polynomial curve fitting. the results show that the flow stress depends strongly on the deformation temperature and the strain rate, and it increases with the deformation temperature decreasing and the strain rate increasing. furthermore, it was found out that the co- existence of δ- ferrite lowers the softening rate at high z (zener- holloman parameter) conditions. the experimental results were then used to determine the constants of constitutive equations. there is a good agreement between the measured and predicted results indicating a high accuracy of exponent- type constitutive equations.
منابع مشابه
Hot Deformation Behavior of 17-7 PH Stainless Steel
To investigate the hot deformation behavior of 17-7 PH stainless steel, hot compression tests were carried out at the temperatures of 950, 1050 and 1150 oC and strain rates of 0.001 s-1 to 0.1 s-1. Accordingly, the hot working behavior was studied by the analyses of flow stress curves, work hardening rate versus stress curves, exponent- type constitutive equations and deformed microstructures. ...
متن کاملDynamic Recrystallization under Hot Deformation of a PH Stainless Steel
Dynamic recrystallization, DRX, behaviour of a precipitation hardened, PH, stainless steel was studied in connection with microstructural developments in a compression test. The experimental results showed that the dominant mechanism of softening is DRX, but at high strain rates and low temperatures, ie, high Zener-Holman parameter, Z, work hardening and dynamic recovery, DRV, produced a pancke...
متن کاملdynamic recrystallization under hot deformation of a ph stainless steel
dynamic recrystallization, drx, behaviour of a precipitation hardened, ph, stainless steel was studied in connection with microstructural developments in a compression test. the experimental results showed that the dominant mechanism of softening is drx, but at high strain rates and low temperatures, ie, high zener-holman parameter, z, work hardening and dynamic recovery, drv, produced a pancke...
متن کاملPREDICTION OF HOT DEFORMATION BEHAVIOUR OF A PH STAINLESS STEEL AT HIGH STRAIN RATES
In this study the hot deformation behaviour of a precipitation hardened (PH) stainless steel at high strain rates has been predicted through hot compression testing. Stress-strain curves were obtained for a range of strain rates from 10-3 to 10+1 S-1 and temperatures from 850 to 1150°C. Results obtained by microstructure and stress-strain curves show that at low temperatures and high strain rat...
متن کاملTowards sustainable machining of 17-4 PH stainless steel using hybrid MQL-hot turning process
The use of a minimum quantity of lubrication (MQL) with extremely low consumption of lubricant in machining processes has been reported as a technologically and environmentally feasible alternative to conventional flood cooling. In hot machining, the external heat source is applied during machining that will assist to increase machining performance. Many external heating techniques are availabl...
متن کاملEVALUATION OF PRECIPITATION HARDENING HEAT TREATMENT OF PH 17-7 STAINLESS STEEL SPRING
In this paper, the influence of heat treatment on PH17-7 stainless steel spring was evaluated. Precipitation hardening phenomenon of PH 17-7 steel was evaluated in three stages. First, the spring constant changes with time and temperature was evaluated. Second, the spring constant changes with respect to its original length at constant temperature and time with blocking (spring length aft...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
iranian journal of materials formingجلد ۴، شماره ۱، صفحات ۱-۱۱
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023