a comparative study on the dispersion of cuo-zno-al2o3 nanoparticles over hzsm-5 via batch co-precipitation, semibatch co- precipitation and combined co-precipitation-ultrasound methods
نویسندگان
چکیده
a series of cuo-zno-al2o3 nanoparticles over hzsm-5 were successfully prepared using different methods of batch co-precipitation, semibatch co-precipitation and combined co-precipitation-ultrasound. nitrates of copper, zinc and aluminum were used as precursors, while na-zsm-5 was employed as composite support and sodium carbonate was used as precipitant agent. the effects of preparation methods on physicochemical properties of synthesized nanoparticles were studied using xrd, bet, fesem, ftir and tga-dtg techniques. furthermore, the formation mechanism of nanosized cuo-zno-al2o3 over hzsm-5 was proposed. the formation of nanosized cuo-zno-al2o3 over hzsm-5 with homogeneous grain size was addressed after calcination at 350°c for 5 hr. the results indicated that the crystalline structure, thermal gravimetric behavior and surface morphology of the nanocomposite were strongly dependent on preparation methods. the combined co-precipitation-ultrasound method had superior control in crystallite size and cuo-zno-al2o3 dispersion. this method resulted in many small grains with almost spherical shapes and narrow particle size distribution.
منابع مشابه
A comparative study on the dispersion of CuO-ZnO-Al2O3 nanoparticles over HZSM-5 via batch co-precipitation, semibatch co- precipitation and combined co-precipitation-ultrasound methods
A series of CuO-ZnO-Al2O3 nanoparticles over HZSM-5 were successfully prepared using different methods of batch co-precipitation, semibatch co-precipitation and combined co-precipitation-ultrasound. Nitrates of copper, zinc and aluminum were used as precursors, while Na-ZSM-5 was employed as composite support and sodium carbonate was used as precipitant agent. The effects of preparation methods...
متن کاملMagnetic Properties of Cobalt Ferrite synthesized by Hydrothermal and Co-precipitation Methods: A Comparative Study
The magnetic properties of calcined cobalt ferrite formed by nano-crystalline powders have been compared by two different methods (co-precipitation and hydrothermal). The structural properties of the produced powders were investigated by X-ray Diffraction (XRD), scanning electron microscopy (SEM). The results show that the formation of cobalt ferrite spinel structures is effected by changing me...
متن کاملSynthesis and characterization of SnO2 nanoparticles by Co-Precipitation method
Tin oxide (SnO2)nanoparticles were synthesized by co-precipitation method and the synthesized nanoparticles were annealed at different temperatures for characterization. The powders were investigated with X-ray diffraction, scanning electron microscopy and optical spectroscopy. The structural characterization was carried out by X-ray diffraction which confirms the crystalline nature ...
متن کاملSYNTHESIS OF AL2O3-NI COMPOSITE POWDERS BY CO-PRECIPITATION METHOD
The synthesis of micro-sized, uniformly distributed Al2O3-15Vol% Ni powders were studied through three step co-precipitation of hydroxides mixtures from proper solution, calcination at air atmosphere and final step of calcined powders in a carbon bed. Al and Ni hydroxide and amorphous phase were first obtained from their salt’s solutions through chemical co-precipitation method by adjusti...
متن کاملComparative synthesis of ZrO2 nanoparticles by green and co-precipitation methods: The effect of template on structure
It was shown that the structure and particle size of zirconia nanoparticles has been controlled through the homogeneous precipitation process by using templates. Hexamine as the template led to ZrO2 nanoparticles with tetragonal structure, whereas coffee extract favored monoclinic structures. Field Emission Scanning electron microscopy (FeSEM), Transmission electron microscopy (TEM) measurement...
متن کاملStructure and Magnetic Properties of Oxide Nanoparticles of Fe-Co-Ni Synthesized by Co-Precipitation Method
Oxide nanoparticles of Fe-Co-Ni were prepared in six different compositions by co-precipitation method. The as-synthesized nanoparticles were characterized by X-Ray Diffraction (XRD), Field Emission Scanning Electron microscope (FESEM), Fourier Transform Infrared (FT-IR) and Vibrating Sample Magnetometer (VSM). It was found that the nanoparticles had mean crystalline size of 30-55 nm and spher...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
chemistry of solid materialsجلد ۱، شماره ۱، صفحات ۰-۰
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023