development of mgal2o4 spinel coating on graphite surface via sol-gel citrate route to improve its water-wettability and oxidation resistance
نویسندگان
چکیده
low water-wettability and oxidation resistance of graphite have limited its application in carbon containing refractory castables. the aims of this study were improvement of water-wettability and the oxidation resistance of natural flaky graphite by applying an oxide coating on its surface. to develop the coating, magnesium aluminate spinel sol was formulated via a citrate-nitrate route and graphite powder was then added to the sol. the mixture was heat treated in appropriate temperature and atmosphere to get the polycrystalline mgal2o4 coating on graphite particles surface. the microstructure of coating was studied by x-ray diffractometer, sem and tem. the water-wettability was evaluated by measuring the water drop contact angle and plotting the zeta potential vs. ph. the results showed the development of a stable nanocrystalline mgal2o4 spinel coating which improved the water-wettability and oxidation resistance of graphite significantly.
منابع مشابه
Preparation and Characterization of ZrO2/ZnO Nanocomposite under Ultrasonic Irradiation via Sol-gel Route
Nanocomposite of ZrO2/ZnO was prepared under ultrasonic irradiation by sol gel process from directly mixing Zirconium and Zinc gels, and the mixture was placed under ultrasonic irradiation for 2 hours then aging time the filtrated composite gel was calcinated at 500°C for 3h in furnace. The precursor sol of zirconium was prepared from an aqueous solution of ZrCl4 and zinc acetate dihydrated was...
متن کاملEffect of Chelating Agent on Morphology and Phase Evolution of Spinel Nanoparticles Synthesized via Sol-Gel Method
The purpose of this study was to evaluate the effect of glycyrol (tri-dentate, GLY) and ethylenediamine (double- dentate clay, en) chelating agents on phase and morphology changes of spinel nanoparticles synthesized by sol-gel method. Characterization of samples was performed by X-ray diffraction (XRD) and field-emission scanning electron microscope (FESEM) equipped with energy dispersive X-ray...
متن کاملEffect of surface roughness on coating SiO2-P2O5-CaO-ZrO2 upon Zirconium by Sol-Gel Method
Zirconium and its alloys have many applications in orthopedic medicine and compared to stainless steel, titanium and other metals used in the manufacture of implants has higher strength and corrosion resistance. Research shows that the method of preparation and surface modification before coating process has a significant impact on improving the metal implants among which include the sandblasti...
متن کاملPreparation and Characterization of ZrO2/ZnO Nanocomposite under Ultrasonic Irradiation via Sol-gel Route
Nanocomposite of ZrO2/ZnO was prepared under ultrasonic irradiation by sol gel process from directly mixing Zirconium and Zinc gels, and the mixture was placed under ultrasonic irradiation for 2 hours then aging time the filtrated composite gel was calcinated at 500°C for 3h in furnace. The precursor sol of zirconium was prepared from an aqueous solution of ZrCl4 and zinc acetate dihydrated was...
متن کاملLOW TEMPERATURE SYNTHESIS OF NANOCRYSTALLINE MgAl2O4 SPINEL VIA SUCROSE PROCESS
Abstract: Nanocrystalline MgAl2O4 spinel powder was synthesized using metal nitrates and a polymer matrix-based composed of sucrose and polyvinyl alcohol (PVA). The precursor and the calcined powders were characterized by simultaneous thermal analysis (STA), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), and scanning electron microscopy (SEM). According to XRD res...
متن کاملPreparation and Characterization of High Specific Surface Area γ-Alumina Nanoparticles Via Sol-Gel Method
In the present investigation, γ-alumina nanoparticles with particle sizes less than 10 nm, high specific surface area (351 m2/g), high pore volumes and relatively narrow pore sizes distribution was prepared via sol-gel method in presence of aluminum isopropoxide as an aluminum precursor, distilled water, acetic acid as hydrolysis rate controller and tert-butanol as solvent. They had meso ...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
نشریه دانشکده فنیجلد ۴۱، شماره ۱۱، صفحات ۰-۰
کلمات کلیدی
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023