dynamic recrystallization kinetics of aisi 403 stainless steel using hot compression test

نویسندگان

e. kevanlo

g.r. ebrahimi

s.a.a. sani

a. momeni

چکیده

in this work dynamic recrystallization behavior of aisi 403 martensitic stainless steel was studied using hot compression tests over temperature range of 900 c -1200 c and strain rate range of 0.001 s-1 - 1 s-1. the obtained flow curves showed that the hot compression behavior of the alloy is controlled by dynamic recrystallization. the flow stress and strain corresponding to the critical, peak and onset of steady state region were related to the zener-hollomon parameter using simple power equations. the variation of dynamic recrystallization fraction with strain showed that restoration kinetics is enhanced with increasing temperature and decreasing strain rate. the development of drx was modeled using avrami kinetics equation. the equations proposed by baragar and cingara-mcqueen were used to develop a new model capable of predicting the flow curves up to the onset of steady state flow region. this work softening is mainly controlled by the phenomenon dynamic recrystallization.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Dynamic recrystallization kinetics of AISI 403 stainless steel using hot compression test

In this work dynamic recrystallization behavior of AISI 403 martensitic stainless steel was studied using hot compression tests over temperature range of 900 C -1200 C and strain rate range of 0.001 s-1 - 1 s-1. The obtained flow curves showed that the hot compression behavior of the alloy is controlled by dynamic recrystallization. The flow stress and strain corresponding to the critical, pe...

متن کامل

Dynamic Recrystallization under Hot Deformation of a PH Stainless Steel

Dynamic recrystallization, DRX, behaviour of a precipitation hardened, PH, stainless steel was studied in connection with microstructural developments in a compression test. The experimental results showed that the dominant mechanism of softening is DRX, but at high strain rates and low temperatures, ie, high Zener-Holman parameter, Z, work hardening and dynamic recovery, DRV, produced a pancke...

متن کامل

Dynamic Recrystallization and Hot Workability of 316LN Stainless Steel

Chaoyang Sun 1,*, Yu Xiang 1, Qingjun Zhou 2, Denis J. Politis 3, Zhihui Sun 1,* and Mengqi Wang 1 1 School of Mechanical Engineering, University of Science and Technology Beijing, Beijing 100083, China; [email protected] (Y.X.); [email protected] (M.W.) 2 Capital Aerospace Machinery Company, Beijing 100076, China; [email protected] 3 Department of Mechanical Engineering, Imperial Co...

متن کامل

dynamic recrystallization under hot deformation of a ph stainless steel

dynamic recrystallization, drx, behaviour of a precipitation hardened, ph, stainless steel was studied in connection with microstructural developments in a compression test. the experimental results showed that the dominant mechanism of softening is drx, but at high strain rates and low temperatures, ie, high zener-holman parameter, z, work hardening and dynamic recovery, drv, produced a pancke...

متن کامل

Dynamic Recrystallization by Necklace Mechanism During Hot Deformation of 316 Stainless Steel

The aim of this study is to investigate the nucleation of new grains by necklacing mechanism during dynamic recrystallization (DRX). The material used is 316 stainless steel. In order to modeling the deformation behavior during hot rolling, one-hit compression tests were performed at temperature range of 950-1100 °C with strain rates of 0.01-1s-1. The result shows that at the tempera...

متن کامل

dynamic recrystallization by necklace mechanism during hot deformation of 316 stainless steel

the aim of this study is to investigate the nucleation of new grains by necklacing mechanism during dynamic recrystallization (drx). the material used is 316 stainless steel. in order to modeling the deformation behavior during hot rolling, one-hit compression tests were performed at temperature range of 950-1100 °c with strain rates of 0.01-1s-1. the result shows that at the temperature of 100...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
iranian journal of materials forming

ناشر: shiraz university

ISSN

دوره 1

شماره Issue 2 2014

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023