effect of nanosilver on the rate of heat transfer to the core of the medium density fiberboard mat
نویسندگان
چکیده
effect of nanosilver (ns) on the heat-transferring rate to the core section of medium density fiberboard (mdf) mat was studied here. a 400 ppm aqueous nanosilver suspension was used at three consumption levels of 100, 150, and 200 ml/kg, based on the weight of dry wood fibers; the results were then compared with the control mdf panels. the size range of nanosilver was 30-80 nm. results showed that the uniform and even dispersion of nanoparticles throughout the mdfmatrix significantly contributed to the faster transfer of heat to the core section. as to the loss of mat water content after the first 3-4 minutes under the hot press, the core temperature slightly decreased in the control panels. however, heat transferring prope rty of nanosilver contributed to keeping the core temperature rather constant in the nanosilver-150 and 200 treatments. the surface layers of the mat rapidly absorbed the heat, resulting in the depolymerization of part of the resin. it can therefore be concluded that the optimum nano suspension content should not necessarily be the highest one.
منابع مشابه
Effect of Nanosilver on the Rate of Heat Transfer to the Core of the Medium Density Fiberboard Mat
Effect of nanosilver (NS) on the heat-transferring rate to the core section of medium density fiberboard (MDF) mat was studied here. A 400 ppm aqueous nanosilver suspension was used at three consumption levels of 100, 150, and 200 mL/kg, based on the weight of dry wood fibers; the results were then compared with the control MDF panels. The size range of nanosilver was 30-80 nm. Results showed t...
متن کاملEffect of Nanosilver on the Rate of Heat Transfer to the Core of the Medium Density Fiberboard Mat
Effect of nanosilver (NS) on the heat-transferring rate to the core section of medium density fiberboard (MDF) mat was studied here. A 400 ppm aqueous nanosilver suspension was used at three consumption levels of 100, 150, and 200 mL/kg, based on the weight of dry wood fibers; the results were then compared with the control MDF panels. The size range of nanosilver was 30-80 nm. Results showed t...
متن کاملthe effect of traffic density on the accident externality from driving the case study of tehran
در این پژوهش به بررسی اثر افزایش ترافیک بر روی تعداد تصادفات پرداخته شده است. به این منظور 30 تقاطع در شهر تهران بطور تصادفی انتخاب گردید و تعداد تصادفات ماهیانه در این تقاطعات در طول سالهای 89-90 از سازمان کنترل ترافیک شهر تهران استخراج گردید و با استفاده از مدل داده های تابلویی و نرم افزار eviews مدل خطی و درجه دوم تخمین زده شد و در نهایت این نتیجه حاصل شد که تقاطعات پر ترافیک تر تعداد تصادفا...
15 صفحه اولthe effect of taftan pozzolan on the compressive strength of concrete in the environmental conditions of oman sea (chabahar port)
cement is an essential ingredient in the concrete buildings. for production of cement considerable amount of fossil fuel and electrical energy is consumed. on the other hand for generating one tone of portland cement, nearly one ton of carbon dioxide is released. it shows that 7 percent of the total released carbon dioxide in the world relates to the cement industry. considering ecological issu...
the effect of creative writing instruction on lexical density of advanced efl learners writing
چکیده ندارد.
15 صفحه اولthe washback effect of discretepoint vs. integrative tests on the retention of content in knowledge tests
در این پایان نامه تاثیر دو نوع تست جزیی نگر و کلی نگر بر به یادسپاری محتوا ارزیابی شده که نتایج نشان دهندهکارایی تستهای کلی نگر بیشتر از سایر آزمونها است
15 صفحه اولمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
international journal of bio-inorganic hybrid nanomaterialsجلد ۲، شماره ۱، صفحات ۳۰۳-۳۰۸
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023