structural and optical properties of gold nanoparticles formed by wet-chemical method
نویسندگان
چکیده
our aim in this work is the synthesis and study optical and structural properties of gold nanoparticles.gold (iii) chloride trihydratewas taken as metal precursor, ascorbic acid at the presence of an appropriate amount of naoh as reducing agent and polyvinylpyrrolidonek-30 (pvp k-30) as a stabilizing and capping agent. the reaction was performed in high-speed stirring rate at room temperature.scanning electron microscopy (sem with edax), x-ray diffraction (xrd) and drs uv-vis analysis have been used for characterization of the sample. sem images shows formation of spherical shape nanoparticles. x-ray diffraction (xrd) measurements showed that the nanoparticles are crystalline and mainly composed of face-centered cubic (fcc). using the debye-scherer formula average particle size of nanoparticles was calculated to be about 4.28 nm. uv-vis absorption spectrum reveals the formation of gold nanoparticles by showing surface plasmon absorption maxima at 500 nm.
منابع مشابه
Structural and Optical Properties of Gold Nanoparticles Formed by Wet-Chemical Method
Our aim in this work is the synthesis and study optical and structural properties of gold nanoparticles.Gold (III) chloride trihydratewas taken as metal precursor, ascorbic acid at the presence of an appropriate amount of NaOH as reducing agent and polyvinylpyrrolidonek-30 (PVP K-30) as a stabilizing and capping agent. The reaction was performed in high-speed stirring rate at room temperature.S...
متن کاملStructural and Optical Properties of Gold Nanoparticles Formed by Wet-Chemical Method
Our aim in this work is the synthesis and study optical and structural properties of gold nanoparticles.Gold (III) chloride trihydratewas taken as metal precursor, ascorbic acid at the presence of an appropriate amount of NaOH as reducing agent and polyvinylpyrrolidonek-30 (PVP K-30) as a stabilizing and capping agent. The reaction was performed in high-speed stirring rate at room temperature.S...
متن کاملcontrol of the optical properties of nanoparticles by laser fields
در این پایان نامه، درهمتنیدگی بین یک سیستم نقطه کوانتومی دوگانه(مولکول نقطه کوانتومی) و میدان مورد مطالعه قرار گرفته است. از آنتروپی ون نیومن به عنوان ابزاری برای بررسی درهمتنیدگی بین اتم و میدان استفاده شده و تاثیر پارامترهای مختلف، نظیر تونل زنی(که توسط تغییر ولتاژ ایجاد می شود)، شدت میدان و نسبت دو گسیل خودبخودی بر رفتار درجه درهمتنیدگی سیستم بررسی شده اشت.با تغییر هر یک از این پارامترها، در...
15 صفحه اولStructural and Optical Behavior of Cu Doped Au Nanoparticles Synthesized by Wet-Chemical Method
The nanoparticles of gold doped with various percentage of copper (Cu 10%, 25%, 75%) were synthesized by wet-chemical method at room temperature. Copper (II) sulfate and gold (III) chloride trihydride was taken as the metal precursor and ascorbic acid as a reducing agent and anhydride maleic as surfactant. The reaction is performed with high-speed stirring at room temperature under nitrogen atm...
متن کاملStructural and Optical Behavior of Cu Doped Au Nanoparticles Synthesized by Wet-Chemical Method
The nanoparticles of gold doped with various percentage of copper (Cu 10%, 25%, 75%) were synthesized by wet-chemical method at room temperature. Copper (II) sulfate and gold (III) chloride trihydride was taken as the metal precursor and ascorbic acid as a reducing agent and anhydride maleic as surfactant. The reaction is performed with high-speed stirring at room temperature under nitrogen atm...
متن کاملInfluence of Different Percentages of Copper on the Size and Optical Properties of Ag-Cu Nanoparticles Formed by Wet-Chemical Method
In this work, Ag-Cu nanoparticles (with different percentages of copper, 10%, 25%, 50%, 75% Cu) were synthesized by wet chemical method. Copper(II) sulfate and silver nitrate were taken as metal precursors, ascorbic acid as reducing agent and anhydride maleic (MA) as a modifier. The prepared nanoparticles were characterized by means of X-ray diffraction (XRD) technique and scanning electron mic...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
international journal of bio-inorganic hybrid nanomaterialsجلد ۳، شماره ۱، صفحات ۱۷-۲۱
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023