hydrogen embrittlement on 2.25cr-1mo steel with ferritic-bainitic & martensitic microstructures
نویسندگان
چکیده
in this paper, effect of hydrogen diffusion on 2.25cr-1mo steel with ferritic-bainitic and martensitic microstructure has been investigated. hydrogen embrittlement of this steel was investigated by doing experimental such as delayed fracture and slow strain rate tests. result of this research was showed that the steel with martensitic microstructure strongly affected by hydrogen diffusion and was embrittled. but same steel with ferritic-bainitic microstructure, even at high level of hydrogen diffusion , has not show any embrittlement. other experiments showed that , if martensitic microstructure steel will be remained on ambient temperature for above one week, effect of hydrogen diffusion will be disappear. in this paper hydrogen embrittlement of 2.25 cr-1mo steel will be discussion
منابع مشابه
Theory for Hydrogen Desorption in Ferritic Steel
After a concise review of the analytical models available for the interpretation of thermal desorption rates for hydrogen effusion from steel, a numerical method that incorporates the essence of local equilibrium and detrapping kinetics has been implemented to account for the real complexity of practical experiments. For example, the model permits the treatment of multiple kinds of traps, uses ...
متن کاملHydrogen embrittlement of ferritic steels: Observations on deformation microstructure, nanoscale dimples and failure by nanovoiding
While hydrogen embrittlement of ferritic steels has been a subject of significant research, one of the major challenges in tackling hydrogen embrittlement is that the mechanism of embrittlement is not fully resolved. This paper reports new observations and interpretation of fracture surface features and deformation microstructures underneath the fracture surface, providing a mechanistic view of...
متن کاملInvestigation on the Enhanced Oxidation of Ferritic/Martensitic Steel P92 in Pure Steam
Oxidation of ferritic/martensitic steel P92 was investigated in pure oxygen and in pure steam at 600-800 °C by thermogravimetric analysis (TGA), optical microscopy (OM), scanning electron microscopy (SEM), and X-ray diffraction (XRD). The results showed that the oxidation of P92 was significantly enhanced and multilayer scale with an outer iron oxides layer formed in pure steam. At 700 °C, the ...
متن کاملAustenite films in bainitic microstructures
Bainitic microstructures in which fine platelets offerrite are intimately mixed with films of austenite are known to exhibit good combinations of strength and toughness. It isfound that the thickness of these austenitefilms can be estimated by assuming that the carbon diffusion field around an existing plate offerrite prevents the close approach of another parallel plate. This is because the re...
متن کاملStrong Ferritic – Steel Welds
There are many steels which are stronger than 2000 MPa, with toughness values exceeding 100 MPa m and which have been in commercial service for many decades. Examples include the marageing alloys and carbide–free bainitic steels. By contrast, welding consumables with a proof strength in excess of 1000 MPa are few and far between. This is because whereas wrought steels can be thermomechanically ...
متن کاملCompatibility of Reduced Activation Ferritic/Martensitic Steels with Liquid Breeders
The compatibility of Reduced Activation Ferritic/Martensitic Steel (RAFM) with liquid Li and molten-salt Flibe have been characterized and accessed. Static compatibility tests were carried out in which the specimens were immersed into liquid Li or Flibe in isothermal autoclaves. Also carried out were compatibility tests in flowing liquid Li by thermal convection loops. In the case of liquid Li,...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
پژوهش نفتجلد ۱۵، شماره ۵۱، صفحات ۶۳-۷۱
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023