synthesis of high isotactic and high melt flow polypropylene in liquid propylene
نویسندگان
چکیده
this is a report on the study of high melt flow, highly isotactic polypropylene homopolymer synthesized in liquid monomer using a fifth generation ziegler-natta catalytic system. at highest catalyst productivity, the response of thecatalyst to hydrogen as chain transfer is studied. melt flow rate is controlled by hydrogen as chain transfer from 0.4 to 300 g/10min with changing the amount of hydrogen from 0 to 1400 ppm. results show that the melt flow rate of homopolymer is increased linearly with increasing the amount of hydrogen in polymerization. the effect of external electron donor on catalyst productivity and stereoregularity of the final product has been studied. the external electron donor on the catalyst caused an increase in polymer isotacticity, but led to decrease in catalyst productivity andits response to hydrogen (i.e., requiring relatively more hydrogen for molecular weight control). this new generation of z-n catalyst system containing 1,3-diether as internal electron donor has the ability to produce very high mfr polymers (for thin wall parts) in combination with narrow molecular weight distribution. these reactor grades of polypropylene have many advantages compared to visbroken (controlled rheology) grades such as lower cost and better processability. these resins can be used as homopolymer matrix in sequential polymerization to obtain impactcopolymers (heterophasic copolymers).
منابع مشابه
High-pressure crystallization of isotactic polypropylene droplets
Dispersions of isotactic polypropylene (PP) particles in polystyrene (PS) were produced by interfacially driven breakup of nanolayers in multilayered systems that were fabricated by means of layer-multiplying coextrusion. The droplet size was controlled by the individual PP layer thickness ranging from 12 to 200 nm. In addition, PP was melt blended with PS to produce PP droplets larger than tho...
متن کاملInfluence of the temperature on flow-induced crystallization of isotactic polypropylene and propylene-ethylene random copolymer
BOITOUT, Hugo, "Influence of the temperature on flow-induced crystallization of isotactic polypropylene and propylene-ethylene random copolymer" (2014). Influence of the temperature on flow-induced crystallization of isotactic polypropylene and propylene-ethylene random copolymer Influence of the temperature on flow-induced crystallization of isotactic polypropylene and propylene-ethylene rando...
متن کاملExtensional-flow-induced crystallization of isotactic polypropylene
A filament stretching extensional rheometer with a custom-built oven was used to investigate the effect of uniaxial flow on the crystallization of polypropylene. Prior to stretching, samples were heated to a temperature well above the melt temperature to erase their thermal and mechanical histories and the Janeschitz-Kriegl protocol was applied. The samples were stretched at extension rates in ...
متن کاملthe relationship between academic self-concept and academic achievement in english and general subjects of the students of high school
according to research, academic self-concept and academic achievement are mutually interdependent. in the present study, the aim was to determine the relationship between the academic self-concept and the academic achievement of students in english as a foreign language and general subjects. the participants were 320 students studying in 4th grade of high school in three cities of noor, nowshah...
Relaxation of Shear-Induced Precursors in Isotactic Polypropylene and Random Propylene-Ethylene copolymers
متن کامل
The Melt Shear Viscosity of Polypropylene/Glass Bead Composites at High Extrusion Flow Rates
The effects of filler content and its surface treatment with silane coupling agent on the melt shear viscosity of glass bead-filled polypropylene (PP) composites have been investigated using a capillary rheometer at a wide shear rate scope of 150 to 7200 s and temperature range of 160 to 200 C. The melt flow obeys power law, but the slopes of the flow curves have transitions at the shear rate o...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
علوم و تکنولوژی پلیمرجلد ۲۰، شماره ۳، صفحات ۲۲۱-۲۲۶
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023