fracture toughness evaluation for brittle polymers under combined tensile-shear loading
نویسندگان
چکیده
fast fracture is one of the major failure modes in brittle polymers. generally, crack growth in these polymers may occur under combined tensile-shear loading. however, the fracture test data reported previously for some dental restorative resins can not be predicted by using the available fracture criteria.in this paper, a modified fracture criterion is used for estimating the fracture load for the mentioned resin samples. it is shown that by considering a more accurate description for the crack tip stresses and also by accounting for the craze zone effects in front of the crack tip, the modified criterion presents significantly better predictions for the fracture resistance in such brittle polymers.
منابع مشابه
investigation of fracture in v-notched brittle polymers under pure shear loading
sudden fracture is one of the major failure modes in brittle materials. plexiglass (polymethyl methacrylate) is a well known brittle polymer, widely used in various industries. many types of notches, particularly v-shaped notches, are sometimes used in the components made of plexiglass. these notches can dramatically decrease the load bearing capacity of components due to the concentration of s...
متن کاملCharacterising the fracture toughness of polymers at moderately high rates of loading with the use of instrumented tensile impact testing
The more common use of instrumentation in impact testing opened up the possibility to apply fracture mechanics testing methods to polymers at moderately high impact rates. Tensile impact testing offers some advantages over the more common three-point bending and compact tension geometries. Most importantly the dynamic effects encountered at (moderately) high impact rates are less significant du...
متن کاملFracture toughness of snow in shear under friction.
The fracture toughness of snow in shear is one of the most relevant parameters when studying the mechanics of snow slab avalanche release. Double-cantilever snow beams were loaded asymmetrically to determine K(IIc). If crack surfaces touch under applied pressure, the fracture toughness in shear of snow (rho=247 kg m(-3)) is K(IIc)=680+/-60 Pa m(1/2). Screening of the stress intensity at the cra...
متن کاملDynamic fracture initiation in brittle materials under combined mode I/II loading
A new test method has been developed to measure the resistance of dynamic fracture initiation in brittle materials under combined mode I/I loadings. The Brazilian disks with center-cracks have been fractured under oblique impact loadings in diarnetral-compression. The dynamic stress intensity factors of mode I and H are evaluated from the superposition integrals of the step response functions f...
متن کاملWrinkling Simulation of Membrane Structures under Tensile and Shear Loading
This paper presents a detailed Finite Element Analysis study of the formation and evolution of wrinkle pattern that observed in stretched thin membranes. The model problem is set up under the various load conditions. As a precondition for wrinkling, development of compressive stresses in the transverse direction is found to depend on both the length-to-width aspect ratio & thickness of the rect...
متن کاملLoading rates and the dynamic initiation toughness in brittle solids
The experimentally determined marked rise of the stress intensity factor required to initiate crack propagation in brittle solids under variably high loading rates, is analyzed. This problem of fracture initiation at the tip of a crack is considered in terms of activating a flaw at some distance away from the tip. By using a semi-infinite crack in an unbounded two-dimensional solid subjected to...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
علوم و تکنولوژی پلیمرجلد ۲۱، شماره ۲، صفحات ۱۰۷-۱۱۷
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023