properties of dental adhesives incorporated with boehmite nano-particles
نویسندگان
چکیده
the incorporation of boehmite nano-particles and its effects on the mechanical properties and bond strength of an experimental dental adhesive were studied.an adhesive solution containing ethanol, bis-gma, tmptma, hema and photo-initiator system (camphorquinone and dmaema) was prepared. silanized boehmite nano-particles were incorporated into the adhesive in different concentrations of 0, 0.2, 0.5, 1, 2, and 5 weight percentages. the suspensions were ultrasonocated to facilitate the nano-particle dispersion. degree of conversion of the adhesive under visible light irradiation was determined using ft-ir spectroscopy. depth of cure, diametral tensile strength, flexural strength, and micro-shear bond strength of the adhesives were measured. scanning electron electron microscopy was utilized to observe the fracture surface topography. the results were compared using one-way anovaand tukey posthoc test at the significance level of 0.05. the results indicated that the diametral tensile strength, flexural strength, and micro-shear bond strength increased at nano-particle contents of 0.2-0.5 wt.% and beyond this range there was a declining trend (p<0.05) observed in all these properties because of the nano-particle agglomeration. no significant difference was observed in flexural moduli of the adhesives with different filler contents. the study revealed that the incorporation of boehmite nanoparticles may improve the properties of dental adhesives.
منابع مشابه
modification of nanoclay for improving the physico-mechanical properties of dental adhesives
هدف اصلی این مطالعه تهیه یک سامانه نوین چسب عاجی دندانی بر پایه نانورس پیوند شده با پلی متاکریلیک اسید، نانورس پیوند شده با پلی اکریلیک اسید، مخلوط نانوسیلیکا و نانورس پیوند شده با پلی متاکریلیک اسید، مخلوط نانوسیلیکا و نانورس پیوند شده با پلی اکریلیک اسید و نانورس پیوند شده با کیتوسان اصلاح شده با گلایسیدیل متاکریلات است. پیوند پلی متاکریلیک اسید و پلی اکریلیک اسید بر ری سطح نانورس در حضور و ...
MECHANICAL PROPERTIES OF DENTAL COMPOSITE MATERIALS REINFORCED WITH MICRO AND NANO-SIZE Al2O3 FILLER PARTICLES
Abstract: Composite specimens were prepared by dispersion of various amounts of nano-sized Al2O3 fillers in a monomer system containing 60% Bis-GMA and 40% TEGDMA. For comparative purposes, composite samples containing micrometer size Al2O3 fillers were also prepared following the same procedure. The mechanical properties of the light- cured samples were assessed by three-point flexural strengt...
متن کاملsynthesis of amido alkylnaphthols using nano-magnetic particles and surfactants
we used dbsa and nano-magnetic for the synthesis of amido alkylnaphtols.
15 صفحه اولMECHANICAL PROPERTIES OF DENTAL COMPOSITE MATERIALS REINFORCED WITH MICRO AND NANO-SIZE Al2O3 FILLER PARTICLES
Composite specimens were prepared by dispersion of various amounts of nano-sized Al2O3 fillers in a monomer system containing 60% Bis-GMA and 40% TEGDMA. For comparative purposes, composite samples containing micrometer size Al2O3 fillers were also prepared following the same procedure. The mechanical properties of the lightcured samples were assessed by three-point flexural strength, diametral...
متن کاملDirective properties of active coated nano - particles
The directivities of the fields radiated by a variety of cylindrical and spherical active coated nano-particles, which are excited by their respective sources of illumination at optical frequencies, are investigated. Particular attention is devoted to the influence of the source location and optical gain constant on the directivities. While significant variations in the directivities are realiz...
متن کاملEffect of zinc-doping in physicochemical properties of dental adhesives.
PURPOSE To evaluate changes in the physicochemical properties, water sorption (WS), solubility (SO), modulus of elasticity (E), ultimate tensile strength (UTS), and microhardness (MH) tests were undertaken in zinc-doped dental adhesives. METHODS Two bonding resins, Adper Single Bond Plus (SB) and Clearfil SE Bond (SEB), were zinc-doped by mixing them with 5, 10 or 20 wt% of ZnO powder, or wit...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
علوم و تکنولوژی پلیمرجلد ۲۳، شماره ۵، صفحات ۴۲۳-۴۳۳
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023