investigation on soda oxygen delignification reaction kinetics of old corrugated container (occ) pulping
نویسندگان
چکیده
the kinetics of old corrugated container (occ) soda-oxygen delignification was investigated. three delignification temperatures (145,165 and 175ºc) were applied. the pulping duration was adjusted at 150 minutes and the measurements were conducted at 10 minutes intervals. the pulping consistency, oxygen pressure and active alkali were constant at 10%, 6 bar and 18% naoh respectively in all pulping trails. at the end of each pulping interval, the kappa number of the pulp was measured, and the kappa number reduction trend was plotted against pulping time. then delignification rates and coefficients of delignification kinetics were calculated. it was revealed that the delignification proceeded in two different phases, called bulk and residual delignification. based on the coordinates of both sections, the intersction point was determined as the transition point from bulk to residual delignification. rate constant coefficient of both bulk and residual delignification are also calculatred. the results of kinetic study showed that when soda-oxygen delignification is applied on occ, the initial phase of the reaction is very fast, but as the delignification proceeds, the rate of delignification is reduced indicating the residual delignification phase. the results showed that in the initial 45 minutes of the reaction, most of the lignin is removed.
منابع مشابه
Extended Delignification of Old Corrugated Container and Totally Chlorine Free Bleaching of the Pulp
The paper industry has taken various steps to address environmental concerns and raw material limitations. Among them, paper recycling has been shown to be a viable option. In this study, the alkaline sulfite pulping of old corrugated containers (OCC) to produce bleachable pulp was investigated. A combination of one of the three active alkali levels (14, 16, and 18%; Na2O, and oven-dry weight o...
متن کاملLow Temperature Soda-Oxygen Pulping of Bagasse.
Wood shortages, environmental pollution and high energy consumption remain major obstacles hindering the development of today's pulp and paper industry. Energy-saving and environmental friendly pulping processes are still needed, especially for non-woody materials. In this study, soda-oxygen pulping of bagasse was investigated and a successful soda-oxygen pulping process for bagasse at 100 °C w...
متن کاملinvestigation on soda and soda- aq pulping of whole kenaf
the present research has been conducted to investigate the soda and soda-anthraquiuone pulping from whole kenaf (v36). in this respect, anatomical characteristics of kenaf bast and core fibers as well as the soda and soda-aq pulp properties produced at four sodium hydroxide concentrations, namely 25, 30, 35 and 40 (g/lit), have been evaluated. the pulping results indicated that pulp yield and k...
متن کاملMultifunctional Alkaline Pulping, Delignification and Hemicellulose Extraction
In this study, multifunctional alkaline pulping was suggested to produce different pulp grades at one mill site, ranging from high-yield paper pulp to high-purity dissolving pulp. In all process modifications, sulfur was successfully replaced by anthraquinone. Autohydrolysis and alkaline pre-extraction were applied to Eucalyptus globulus wood chips, followed by kraft and soda-AQ pulping. Alkali...
متن کاملRice Husk and Old Corrugated Container Cement Boards: Performance of Nano-SiO2 on Strength and Dimensional Stability
In this study the effect of nano sized silica particles (nano-SiO2) on the physical and mechanical properties of rice husk and Old Corrugated Container (OCC)-cement boards was investigated. Modulus Of Rupture (MOR), Modulus Of Elasticity (MOE), Internal Bonding Strength (IB), density, water absorption and thickness swelling after 24 hours immersion in water and hardness were meas...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
جنگل و فرآورده های چوبجلد ۶۹، شماره ۱، صفحات ۲۱۵-۲۲۴
کلمات کلیدی
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023